5um Ceramic Fiber Blanket High Working Temperature 280kg / M3 Insulation
1260 Degree Ceramic Fiber Blanket High Working Temperature 96-280kg/M3 Insulation
The ceramic fiber board is made from refractory fiber by adding suitable binders through wet suction vacuum molding process. It has good performance on size, roughness, and radian, and has the characteristics on high strength, low thermal conductivity, good thermal shock resistance and spalling resistance. It can be easily cut and installed, and can widely be used for kiln, furnace, and other high temperature equipment.
CH Refractories manufacturered Refractory ceramic fiber board is customized, size can be made accordind to requirements.
| Product code | CH-XWK40 | CH-XWK45 | CH-XWK48 | CH-XWK50 | CH-XWBZ15 |
| Material | Aluminum silicate | High alumina | Zirconia contained | ||
| Al2O3% | 40-44 | 44-46 | 46-50 | 50-60 | 30-35 |
| Al2O3+Si02% | ≥94 | ≥97 | ≥98 | ≥98 | ≥98 (+Zr02) |
| ZrO2% | - | - | - | - | ≥15 |
| Fe2O3% | ≤1. 2 | ≤1.0 | ≤0.8 | ≤0.5 | ≤0.5 |
| Na2O+K2O% | ≤0.5 | ≤0.5 | ≤0.2 | ≤0.2 | ≤0.2 |
| Service temperature ℃ | ≤1000 | ≤1000 | ≤1100 | ≤1200 | ≤1350 |
|
Volume density /kg.m3
|
200~600 | 200~600 | 200~600 | 200~600 | 200~600 |
|
Thermal conductivity /W(m.k)
|
≤0.14 (600℃) ≤0.18 (800℃) |
≤0.14 (600℃) ≤0.18 (800℃) |
≤0.18 (800℃) ≤0.22 (1000℃) |
≤0.18 (800℃) ≤0.22 (1000℃) |
≤0.88 (1000℃) ≤0.28 (1200℃) |
|
Heating shrinkage ／％ |
≤1.5 (900℃,24H) |
≤1.5 (1000℃,24H) |
≤1.5 (1100℃,24H) |
≤1.5 (1200℃,24H) |
≤1.5 (1300℃,24H) |
| General size |
600mmX400mmX(10-50)mm 900mmX600mmX(10-50)mm
|
||||
Advantages of Refractory ceramic fiber board
*Lightweight and low thermal conducitivty
*High working temperature resistance and insulation
*Superior strength for easy installation and maintenance
*Low fiber shot contents and high resilience
*Low heat storage for high efficiency enery savings
*Can be foled, compressed for modules or blocks as insulation