CuCo2Be C17500 Beryllium Copper Rod Outer Diameter 0.06-2.00mm
CuCo2Be Cobalt Beryllium Copper Rod Out Diameter 0.06-2.00mm For Electrical Industry
CUBERYLLIUM® manufactures copper beryllium in several distinct compositions. These fall into two categories: alloys selected for high strength (Alloys 172,173,170) and alloys selected for high conductivity (Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia Market. Also Supply Master alloy : CuBeryllium-200; CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global factory.
C17500 Beryllium Copper Rod Specification
| Name | C17500 Beryllium Copper Rod, CuCo2Be Cobalt Copepr Rod, Alloy 10 Copper Rod |
| Standard of Rod | ASTM B441, SAE J461, 463; RWMA Class 3 |
| Different Shape | We offer C17500 Rods/Bars in various shapes, sizes, strandards and grades to offer wide customization options to our customers. |
| Processing | Seamless / Welding |
| Application |
A: Electrical Industry: Switch Parts, Connectors, Spring Connectors, Fuse Clips, Relay Parts; B: Fasteners: Washers, Fasteners; C: Industrial: Spring, Resistance Welding Equipment, Resistance and Spot Welding Tips, Seam Welding Dies, Die-Casting Plunger Tips, Tooling for Plastic Moulds. |
Chemical Composition of CuCo2Be Cobalt Beryllium Copper Alloy:
| CUBERYLLIUM® Brand | UNS-Number | Beryllium | Cobalt | Nickel | Cobalt+Nickel | Lead | Copper |
| Cuberyllium-C750 | C17500 | 0.40-0.70 | 2.4～2.7 | - | - | - | Balance |
Typical Physical Properties of CuCo2Be Cobalt Beryllium Copper Alloy:
| Density | 8.83 | g/cm3 |
| Density before age hardening | 8.75 | g/cm3 |
| Melting Range | 1000~1070 | ℃ |
| Elastic Modulus | 14.1 | (kg/mm2 (103) |
| Thermal Expansion Coefficient | 18 x 10 -6 | 20 °C to 200 °C m/m/°C |
| Thermal Conductivity | 0.48 | cal/(cm-s-°C) |
Mechanical and Electrical Properties of Copper Beryllium Rod&Bar and Tube of CUBERYLLIUM®-750:
| Temper(*) | Diameter | Heat Treatment |
Tensile Strength Mpa |
Elongation Percent (Min) |
Electrical Conductivity Percent IACS |
Hardness Rockwell B Scale |
|---|---|---|---|---|---|---|
| A(TB00) | ALL SIZE | / | 240~380 | 20~40 | 20~35 | B20~50 |
|
H(TD04) |
ALL SIZE | / | 440~550 | 10~20 | 20~35 | B20~30 |
| AT(TF00) | ALL SIZE | 3 hr 480℃ | 680~900 | 10~30 | 45~60 | B92~100 |
| HT(TH04 | ALL SIZE | 2 hr 480 ℃ | 750~960 | 5~30 | 48~60 | B95~102 |
Product Photo:
Weldability
Soldering, brazing, gas shielded arc welding, coated metal arc welding, spot welding, seam welding and butt welding are all recommended
Hot & Cold Workability
Good hot working properties. Excellent cold working properties.
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.
FAQ:
Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?
A1: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid before the delivery.
Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.