CuBe2 C17200 Beryllium Copper Strip Thickness 0.28mm With State XHM
CuBe2(C17200) Thickness 0.28mm Beryllium Copper Strip With State XHM and Hardness 300~360HV
Product Normal Description:
Product Name: Beryllium copper strip
Grade: CuBe2(C17200)
Standard: ASTM B194, SAE J463, J461
Product Specification: 0.28mmx100mm
State: XHM
Product Brand: CUBERYLLIUM®
Chemical Composition of CuBe2(C17200) Beryllium Copper Alloys:
Beryllium(Be): 1.80-2.00%
Cobalt(Co) + Nickel(Ni): 0.20% Min
Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max
Lead: 0.02% Max
Copper(Cu): Balance
Note: Copper plus additions equal 99.5% Minimum.
The principle characteristics of alloy 172 are an excellent response to precipitation-hardening treatments, excellent thermal conductivity, and resistance to stress relaxation. The high strength beryllium coppers C172 can be purchased in the solution annealed or cold worked tempers and can be easily formed or machined. A low-temperature heat treatment (600 degrees for 2-3 hours) produces maximum strength and hardness. C17200, also commonly known as Alloy 25, CuBe2, is available in round rod, bar, tube, strip, and wire.
| CuBe2(C17200) Strip Application: | Electrical |
|---|---|
| Fasteners | |
| Industrial | |
| Connectors, contacts | |
| Bushings/bearings for aerospace industry | |
| Oilfield drilling collars and instrument housing | |
| Springs | |
| Rugged resistance welding gun structural components | |
| Plastic injection molding and metal diecastings |
Typical Physical Properties of CuBe2(C17200) Beryllium Copper Alloys:
| Density (g/cm3): | 8.36 |
| Density before age hardening (g/cm3): | 8.25 |
| Elastic Modulus (kg/mm2 (103)): | 13.4 |
| Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): | 17 x 10-6 |
| Thermal Conductivity (cal/(cm-s-°C)): | 0.25 |
| Melting Range (°C): | 870-980 |
Temper Designations of CuBe2(C17200) Beryllium Copper Strip:
| Cuberyllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Strip | ||||||
| Designation | Description | Tensile Strength (Mpa) |
Yield Strength 0.2% offset | Elongation Percent | HARDNESS (HV) |
HARDNESS Rockwell B or C Scale |
Electrical Conductivity (% IACS) |
|
| A | TB00 | Solution Annealed | 410～530 | 190～380 | 35~60 | <130 | 45~78HRB | 15～19 |
| 1/2 H | TD02 | Half Hard | 580～690 | 510～660 | 12~30 | 180~220 | 88~96HRB | 15～19 |
| H | TD04 | Hard | 680~830 | 620~800 | 2~18 | 220~240 | 96~102HRB | 15～19 |
| HM | TM04 | Mill hardened |
930～1040 | 750～940 | 9～20 | 270～325 | 28～35HRC | 17～28 |
| SHM | TM05 | 1030～1110 | 860～970 | 9～18 | 295～350 | 31～37HRC | 17～28 | |
| XHM | TM06 | 1060～1210 | 930～1180 | 4～15 | 300～360 | 32～38HRC | 17～28 | |
Product Package of Beryllium Copper Alloys:
Usually we pack the beryllium copper strips on coil, outside is plywood case.
Why Choose Us?
1, We are a professional beryllium copper alloy manufacturer, with more than 20 years' experience.
2, With various types of beryllium copper alloy, such as beryllium rods, bars, strips, wires and so on.
3, Good quality.
4, Competitive offers.
5, After-sale service.
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.