0.4mm Diameter Beryllium Wire CuBe2 ASTM B197 Standard
CuBe2 Wires 0.4mm Diameter ASTM B197 Standard With Good Properties of Beryllium
| Commodity | CuBe2 Wires |
| Grade | CuBe2, ASTM B196 |
| Dia. | 0.4mm |
| Length | we also could cut any length according customers' demand |
| Surface | Bright, Polished |
| Package | Pack in woodencase |
| State | TB00 |
| Product Brand | CUBERYLLIUM® |
Introduction of CuBe2 Alloys:
CuBe2- – C17200 (CDA 172) Beryllium Copper is the most normally used Copper Beryllium compound and is eminent for its most elevated quality and hardness contrasted with business copper composites. We are one of the biggest suppliers, manufacturer, exporter of beryllium copper wire. Beryllium copper wire widely used in the electrical industry, fasteners, and other various industries such as the electrochemical industry, pumps, springs, etc.. C17200 contains appr. 2% of beryllium and accomplishes its definitive elasticity can surpass 200 ksi, while the hardness approaches Rockwell C45. In the meantime, the electrical conductivity is at least 22% IACS in the completely matured condition.C17200 likewise displays remarkable protection from stress unwinding at raised temperatures. Cuberyllium supplies beryllium copper wire, CuBe2 beryllium copper wire, UNS.C17200 beryllium copper wire as per customer’s requirements.
Chemical Composition of CuBe2 Alloy:
Product Grade: CUBERYLLIUM ®-172(UNS. C17200)
Beryllium(Be): 1.80-2.00%
Cobalt(Co) + Nickel(Ni): 0.20% Min
Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max
Lead: 0.02% Max
Copper(Cu): Balance
Note: Copper plus additions equal 99.5% Minimum.
Typical Physical Properties of CuBe2 Alloy:
| Density (g/cm3): | 8.36 |
| Density before age hardening (g/cm3): | 8.25 |
| Elastic Modulus (kg/mm2 (103)): | 13.4 |
| Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): | 17 x 10-6 |
| Thermal Conductivity (cal/(cm-s-°C)): | 0.25 |
| Melting Range (°C): | 870-980 |
Mechanical and Electrical Properties of CuBe2 Wires:
| Alloy | Temper (*) | Heat Treatment | Tensile Strength Mpa | Elongation percent | Electrical Conductivity percent IACS |
| CUBERYLLIUM 172 |
A | / | 400～580 | 30-60 | 15-19 |
| (TB00) | |||||
| 1/4 H | / | 570～795 | 3~25 | 15-19 | |
| (TD01) | |||||
| 1/2 H | / | 710～930 | 2~15 | 15-19 | |
| (TD02) | |||||
| 3/4 H | / | 840～1070 | 2~8 | 15-19 | |
| (TD03) | |||||
| H | / | 915～1140 | 1~6 | 15-19 | |
| (TD04) | |||||
| CUBERYLLIUM 172 |
AT | 3 hr 315℃ | 1050~1380 | 3 min | 22-28 |
| (TF00) | |||||
| 1/4 HT | 2 hr 315℃ | 1150~1450 | 2 min | 22-28 | |
| (TH01) | |||||
| 1/2 HT | 1.5hr 315℃ | 1200~1480 | 2 min | 22-28 | |
| (TH02) | |||||
| 3/4 HT | 1.0 hr 315℃ | 1250~1585 | 2 min | 22-28 | |
| (TH03) | |||||
| HT | 1.0hr 315℃ | 1300~1585 | 1 min | 22-28 | |
| (TH04) |
Product Photo:
Process of Copper Beryllium Wires:
FAQ:
Q1:Could you produce Beryllium Copper strip by Mill Hardened process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06) XHMS(TM08).,we are the only factory could do harden strip in China.
Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.