Beige wear-resistant oil-bearing mc nylon sheet PA66 General Engineering Plastics
The reason for the deformation of nylon parts is that it has high moisture absorption, and it can be placed in cold water to shape it immediately after being ejected from the mold. The post-treatment method is generally to use potassium acetate and boiling water to adjust the humidity to solve the deformation and internal stress, and then lathe processing, the ratio of potassium acetate to water is 1.25 to 1.
| Property | Item No. | Unit | MC Nylon (Natural) | Oil Nylon+Carbon (Black) | Oil Nylon (Green) | MC901 (Blue) | MC Nylon+MSO2 (Light black) |
| 1 | Density | g/cm3 | 1.15 | 1.15 | 1.135 | 1.15 | 1.16 |
| 2 | Water absorption (23℃ in air) | ％ | 1.8-2.0 | 1.8-2.0 | 2 | 2.3 | 2.4 |
| 3 | Tensile strength | MPa | 89 | 75.3 | 70 | 81 | 78 |
| 4 | Tensile strain at break | ％ | 29 | 22.7 | 25 | 35 | 25 |
| 5 | Compressive stress(at 2%nominal strain) | MPa | 51 | 51 | 43 | 47 | 49 |
| 6 | Charpy impact strength (unnotched) | KJ/m2 | No break | No break | ≥50 | No BK | No break |
| 7 | Charpy impact strength (notched) | KJ/m2 | ≥5.7 | ≥6.4 | 4 | 3.5 | 3.5 |
| 8 | Tensile modulus of elasticity | MPa | 3190 | 3130 | 3000 | 3200 | 3300 |
| 9 | Ball indentation hardness | N2 | 164 | 150 | 145 | 160 | 160 |
| 10 | Rockwell hardness | - | M88 | M87 | M82 | M85 | M84 |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Guangzhou Engineering Plastics Industries Co., Ltd.
Location
Building C2, Shuangsha Industrial Area, No.38 Fuda Rd., Huangpu district, Guangzhou, China.
Contact Person
Action xu