430 Stainless Steel Sheet Plate 6000mm Board Coil Strip
Stainless steel sheet 304l 316 430 stainless steel plate S32305 904L stainless steel sheet plate board coil strip
|
A.I.S.I.
U.N.S. |
Characteristics
|
End-Use
|
|
301
S30100 |
Able to attain tempers from 1⁄4 through full
hard, extra full hard by cold rolling. Withstands severe forming in annealed condition. |
Kitchen sinks, Automotive wheel
covers. Toaster springs, Seat belt buckles |
|
303
S30300 |
Highest machinability rating among the
300 series. Forming and welding are not recommended. |
Nuts and bolts, threaded rods,
Fittings. |
|
304
S30400 |
Excellent corrosion resistance and suitable
for deep drawing applications when Nickel content is increased. Carbon content .08% max. |
Food Industry, Chemical Industry,
Deep drawing applications, Aesthetic application. |
|
304L
S30403 |
Same characteristics as 304 with a lower
carbon content .03% max. Used when post weld annealing is impossible. The lower carbon content reduces carbide precipitation in the welded zone. |
Large fabricated equipment.
|
|
316
S31600 |
Molybdenum bearing alloy with better
overall corrosion resistance than 304 and higher creep strength at elevated temperatures. |
Marine coastal environments, Pulp
and paper industry, Chemical and petrochemical Industry |
|
316L
S31603 |
Same characteristics as 316 with a lower Carbon content .03 max. Good corrosion resistance in high temperature intermittent
service. Used when post weld annealing is impossible. The lower carbon content reduces Carbide precipitation in the welded zone. |
Large fabricated equipment.
|
|
317L
S31703 |
Higher Molybdenum content than 316 for
better corrosion resistance. Carbon con tent .03% max. |
Corrosive environments. Chemical
and petrochemical industries. |
|
309
S30900 309S S30908 |
Heat resisting alloy with good corrosion
resistance. High tensile and creep strengths as well as at elevated temperatures. 309S has a lower Carbon content .03 max. |
Furnace parts, Baffles, Cement kiln
chains. Exhaust manifold butterfly valves. |
|
310
S31000 310S S31008 |
Improved characteristics over 309 and
better scaling resistance in intermittent elevated temperatures. Grade 310 has a low co-efficient of expansion. |
Furnace parts, Carburizing boxes,
Heat exchangers, Oil burner parts. |
FAQ
Q1:What is your terms of payment?
A:We usually accept T/T in advance, L/C for large sum.If you prefer other payments terms, please discuss.
Q2:What is your delivery time?
A:For products in stock, we can ship it within 7 days after receiving the deposit. For customer order, production time is 15-30 workdays after receiving the deposit.
Q3:Can I place an sample order and what is your MOQ if I accept your quality?
A:Yes, we can send you samples but you may pay the express fees and customized samples will take about 5-7days, our MOQ is 1 ton.
Q4:How could you guarantee your products?
A:Mill Test Certification is supplied with shipment, We also accept and support the third-party inspection.We also could issue the warranty to customer to guarantee the quality.
Q5:How can I get the price of needed product?
A:It's the best way if you can send us the material, size and surface, so we can produce for u to check the quality.If you still have any confusion, just contact us, we would like to be helpful.
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.