NdFeB Injection Magnetic Compound Isotropic Bonded Neodymium Magnet Particles
Price:
USD 20-80USD/KG
MOQ:
1 Bag
Delivery Time:
1-2 weeks
Brand:
MGT
Product Description
Isotropic Bonded Neodymium Magnet Particles NdFeB Granules Injection NdFeB Compound
Process flow
- 1. Use NdFeB magnetic powder to mix with PA6 or PA12 or PPS or EPA, antioxidants and lubricants, and form pellets in a screw extruder
- 2.The granules are sieved and weighed, and the properties are measured and then packed into buckets or bags, and packed on pallets
Application
- Injection molding NdFeB compouds are a kind of bonded NdFeB products, and are suitable for products formed by injection molding machines. Because of the high precision of injection molding and integrated molding with copper, stainless steel, plastic bearings and other types of inlays, It can be used in micro motors, motor rotors and sensors, automotive motors, and can also be used in household appliances and toys
Feature
- Advantages of precise dimensions, light weight, thin walls and complex shapes
- Stable magnetic properties, can be bonded together with other metal parts
- In many electronic products with high precision and high performance requirements, injection molding magnets can meet their requirements
| ISO NdFeB/PA12 Compound for Injection 2022.5.8 | |||||||||||||||
| HCNT240L | HCNT240LL | HCNT245LL | HCNT250LL | HCNT250BL | HCNT250L | HCNT255HHL | HCNT2599L | HCNT260L | HCNT260BL | HCNT270L | HCNT280L | ||||
| 单位Unit | |||||||||||||||
| Magnetic Properties | Residual Induction | Br | mT | 400-560 | 410-450 | 460-520 | 470-550 | 470-550 | 470-550 | 480-560 | 510-590 | 510-590 | 510-590 | 560-620 | 600-650 |
| kGs | 4.0-5.6 | 4.1-4.5 | 4.6-5.2 | 4.7-5.5 | 4.7-5.5 | 4.7-5.5 | 4.8-5.6 | 5.1-5.9 | 5.1-5.9 | 5.1-5.9 | 5.6-6.2 | 6.0-6.5 | |||
| Coercive Force | Hcb | kA/m | 183-318 | 247-310 | 310-342 | 310-367 | 310-366 | 310-366 | 334-398 | 334-382 | 334-382 | 334-382 | 358-414 | 366-422 | |
| kOe | 2.3-4.0 | 3.1-3.9 | 3.9-4.3 | 3.9-4.6 | 3.9-4.6 | 3.9-4.6 | 4.2-5.0 | 4.2-4.8 | 4.2-4.8 | 4.2-4.8 | 4.5-5.2 | 4.6-5.3 | |||
| Intrinsic Coercivity | Hcj | kA/m | 270-772 | 573-732 | 597-717 | 636-733 | 636-732 | 637-732 | 1034-1354 | 636-732 | 653-732 | 636-732 | 677-772 | 597-716 | |
| kOe | 3.4-9.7 | 7.2-9.2 | 7.5-9.0 | 8.0-9.2 | 8.0-9.2 | 8.0-9.2 | 13.0-17.0 | 8.0-9.2 | 8.2-9.2 | 8.0-9.2 | 8.5-9.7 | 7.5-9.0 | |||
| Max.BH | (BH)max | kJ/cm3 | 27.8-35.8 | 28-36 | 36.1-41.4 | 39.8-46.2 | 35.8-42.2 | 40-46 | 39.8-51.8 | 43-46 | 46-52 | 46.1-49.5 | 52-60 | 59-68 | |
| MGOe | 3.5-4.5 | 3.5-4.6 | 4.6-5.2 | 5.0-5.8 | 5.3-5.7 | 5.0-5.8 | 5.0-6.5 | 5.5-5.8 | 5.8-6.5 | 5.8-6.2 | 6.5-7.5 | 7.5-8.5 | |||
| Physical Properties | 密度Density | ρ | g/cm3 | 5.2-5.35 | 4.5-4.6 | 4.4-4.6 | 4.9-5.3 | 5.0-5.3 | 4.9-5.3 | 5.0-5.5 | 5.2-5.35 | 4.9-5.3 | 5.15-5.2 | 4.9-5.3 | 5.3-5.6 |
| Melt Flowrate | MFR | g/10min | 300-500 | 300-500 | 120-350 | 300-500 | 300-500 | 300-500 | 300-500 | 300-500 | 450-650 | 300-500 | 450-650 | 300-500 | |
| (270℃ 5kg) | |||||||||||||||
| Shrinkage | % | 0.3-0.5 | 0.9-1.1 | 0.7-1.0 | 0.3-0.5 | 0.3-0.5 | 0.3-0.5 | 0.3-0.5 | 0.3-0.5 | 0.3-0.5 | 0.3-0.5 | 0.3-0.5 | 0.1-0.3 | ||
| Tensile Stength | ASTM-D638 | MPa | 47 | 57 | 55 | 46 | 43 | 48 | 44 | 48 | 42 | 46 | 45 | 35 | |
| Flexural Modulus | ASTM-D790 | MPa | 85 | 110 | 105 | 86 | 84 | 84 | 83 | 89 | 85 | 84 | 88 | 65 | |
| Flexural Modulus | ASTM-D790 | Gpa | 15 | 12 | 12 | 14 | 15 | 15 | 15 | 15 | 15 | 15 | 15 | 18 | |
| ZOD Impact Strength | ASTM-D256 | (kJ/m2) | 8 | 10 | 11 | 10 | 8.5 | 8 | 8.8 | 8.6 | 8.4 | 8.2 | 8.5 | 6.4 | |
| 射出成型条件 | |||||||||||||||
| LT-35T (35ton ) Ring Φ10xΦ7x10 | Predrying | ℃/hr | 80/4 | ||||||||||||
| Barrel Temp. | T1 (加料) |
℃ | 230 | 230 | 230 | 230 | 230 | 230 | 230 | 230 | 230 | 230 | 250 | 250 | |
| T2 | ℃ | 245 | 245 | 245 | 245 | 245 | 245 | 245 | 245 | 245 | 245 | 270 | 270 | ||
| T3 (料嘴) |
℃ | 250 | 250 | 250 | 250 | 250 | 250 | 250 | 250 | 250 | 250 | 275 | 275 | ||
| Mold Temp. | ℃ | 80 | 80 | 80 | 80 | 80 | 80 | 80 | 80 | 80 | 80 | 80 | 80 | ||
| Pressure | MPa (kg/cm2) |
94 (959) |
82.25 (839) |
105.8 (1079) |
94 (959) |
70.5 (719) |
94.0 (959) |
117.5 (1198) |
94.0 (959) |
94.0 (959) |
94.0 (959) |
105.7 (1079) |
94.0 (959) |
||
| Speed | % | 60 | 60 | 60 | 60 | 60 | 60 | 60 | 60 | 60 | 60 | 80 | 60 | ||
| 1. Molding conditions for customers'reference, the highest temperature of nylon injection barrel is not allowed to exceed 280 degrees. | |||||||||||||||
| 2. It can be customized according to customers'requirements | |||||||||||||||
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Qingdao Magnet Magnetic Material Co., Ltd.
Location
NO.3 Building, NO.12 LiaoYang East Road, LaoShan District, QingDao, China
Contact Person
Jack Cui