factory ASTM B265 Gr5 Titanium Foil Sheet Acid Pickling width 200mm
Price:
21-48USD/Kg
MOQ:
10kg
Delivery Time:
15-25Days
Brand:
CSTY
Product Description
ASTM B265 Grade 5 Titanium Alloy Sheet
1. Titanium plate advantage:
1. Titanium plate is the surface of the oxide film is equivalent to a good long-term wear-resistant release agent, the use of titanium plate to save the separation agent, so that easy to peel off the plate, eliminating the pre- treatment process, The board is lighter than the copper plate.
2. Titanium plate of the life of copper plate is more than 3 times, according to operating conditions up to 10 to 20 years
3. With titanium plate made of electrolytic copper crystal structure dense, smooth surface, excellent quality.
4. Since the titanium plate does not need to apply the separating agent, it can avoid the pollution of the copper electrolyte.
5. To improve production capacity to reduce the cost of electrolytic copper production,which has a better economic benefits.
3. With titanium plate made of electrolytic copper crystal structure dense, smooth surface, excellent quality.
4. Since the titanium plate does not need to apply the separating agent, it can avoid the pollution of the copper electrolyte.
5. To improve production capacity to reduce the cost of electrolytic copper production,which has a better economic benefits.
2. Process introduction:
Hot rolling : the process of rolling at temperatures higher than those of recrystallization.
The rolling process in which the plastic deformation temperature of a cold rolling is lower than the recovery temperature.
Annealing: a process in which metals are heated slowly to a certain temperature, held for a sufficient time, and then cooled (usually slowly, sometimes by controlled cooling) at an appropriate rate.
Pickling: to immerse the parts in an aqueous solution of sulfuric acid, etc., so as to remove the oxide and other thin films on the surface of the metal.Is the plating, enamel, rolling process such as pre - or intermediate treatment.
The rolling process in which the plastic deformation temperature of a cold rolling is lower than the recovery temperature.
Annealing: a process in which metals are heated slowly to a certain temperature, held for a sufficient time, and then cooled (usually slowly, sometimes by controlled cooling) at an appropriate rate.
Pickling: to immerse the parts in an aqueous solution of sulfuric acid, etc., so as to remove the oxide and other thin films on the surface of the metal.Is the plating, enamel, rolling process such as pre - or intermediate treatment.
3 Physical and chemical properties :
|
Chemical composition |
|||||||||
|
Grade |
N |
C |
H |
Fe |
O |
Al |
V |
Pa |
Ti |
|
Gr2 |
0.03 |
0.08 |
0.015 |
0.3 |
0.25 |
/ |
/ |
/ |
Remain |
|
Gr5 |
0.05 |
0.08 |
0.015 |
0.4 |
0.2 |
5.5~6.75 |
3.5~4.5 |
/ |
Remain |
|
Gr7 |
0.03 |
0.08 |
0.015 |
0.3 |
0.25 |
/ |
/ |
0.12~0.25 |
Remain |
|
Gr9 |
0.03 |
0.08 |
0.015 |
0.25 |
0.15 |
2.5~3.5 |
2.0~3.0 |
/ |
Remain |
|
Mechanical Property |
|||||
|
Grade |
Tensile strength |
Yeild strength |
Elongation |
||
|
|
MPa |
kis |
ksi Mpa |
ksi Mpa |
% |
|
Gr 2 |
345 |
50 |
40(275) |
65(450) |
20 |
|
Gr 5 |
895 |
130 |
828 |
120 |
10 |
|
Gr 7 |
345 |
50 |
40(275) |
65(450) |
20 |
|
Gr 9
|
620
|
90
|
70(483)
|
...
|
15
|
4. Production Specification:
| Cold -rolling plate (Y state) | Thickness(0.3-0.4mm)×Width(400-2000mm)×L mm |
| Hold-rolling plate(R State ) | Thickness(4.0-30mm)×Width(400-3000mm)×L9000mm |
| Foil/Strip | Thickness(0.1-6.0mm )×Width(100-1500mm)×L mm |
| Surface | Acid picklingor Polished |
| Grade we can offer | Gr1 Gr2 Gr5 Gr7 Gr9 Gr12 |
| Standard we can offer | ASTM B265. ASTM F136 .ASTM F67 .AMS4911 .ASTM B38 |
Tag:titanum alloy sheet factory,china titanium plate,titanum sheet price ,ASTM B265 titanium plate,manufacturer titanium sheet
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Baoji City Changsheng Titanium Co.,Ltd
Location
No.26 Baotai Road, Weibin District, Baoji City
Contact Person
Feng