ISO BV 430 Stainless Steel Coil Corrosion Resistance Hot Rolled 2mm 5mm Thick
ISO BV 430 Stainless Steel Corrosion Resistance Hot Rolled 2mm 5mm Thick Coil
|
Description:
Stainless Steel 430 1.4016 This data sheet applies to stainless steel 430 / 1.4016 hot and cold-rolled sheets/plates and strips,semi-finished products, rods, wire, sections and bright products for general purpose. ApplicationRail and road vehicles, container building, warehouse and transport devices for the sugar industry, sound absorber, coal mining. The steel is resistant to intergranular corrosion. ProcessingCold forming with low amount of deformation is easily feasible above room temperature. Sharp chamfers parallel to the direction of rolling have to be avoided. Sheets with greater thicknesses and/or higher amount of deformation should be preheated up to 200 - 400 °C. If applicable, a hot forming at 700 - 900 °C can be necessary. The corrosion resistance is affected by annealing colors, which occur after hot forming or welding, or scalings. These have to be removed by pickling (pickling solution), grinding or sand blasting. It is only allowed to use iron-free tools for these workings. Machining does not differ from machining of non-alloy carbon steels with comparable or corresponding strength. RemarkAccording to DIN EN 10095, appendix D material 1.4016 is deemed to be heat resisting. |
|
Chemical Compositions
| Element | % Present (in product form) | |
|---|---|---|
| C, H, P | L | |
| Carbon (C) | ≤0.08 | ≤0.08 |
| Silicon (Si) | ≤1.00 | ≤1.00 |
| Manganese (Mn) | ≤1.00 | ≤1.00 |
| Phosphorous (P) | ≤0.040 | ≤0.040 |
| Sulfur (S) | ≤0.015 | ≤0.0301) |
| Chromium (Cr) | 16.00 - 18.00 | 16.00 - 18.00 |
| Iron (Fe) | Balance | Balance |
Mechanical properties (at room temperature in annealed condition)
| Product Form | Thickness t or diameter4) d mm max | Yield Strength Rp0.2 | Tensile Strength | Elongation min. in % | |
|---|---|---|---|---|---|
| N/mm2 (longitudinal) |
N/mm2 (transverse) |
Rm N/mm2 | A80mm1) ˂3mm thickness (longitudinal and transverse) | ||
| C | 8 | 260 | 280 | 450 - 600 | 20 |
| H | 13.5 | 240 | 260 | 450 - 600 | 18 |
| P | 252) | 240 | 260 | 430 - 630 | 20 |
| L3) | 100 | 240 | - | 400 - 630 | 20 (longitudinal) |
Minimum values of the 0.2 %-Yield strength of ferritic steels at elevated temperatures
| Product | Heat Treatment Condition | 0.2 %-Yield strength at the temperature °C | ||||||
|---|---|---|---|---|---|---|---|---|
| 100 | 150 | 200 | 250 | 300 | 350 | 400 | ||
| C, H, P, L | Annealed | 220 | 215 | 210 | 205 | 200 | 195 | 190 |
Reference data on some physical properties
| Density at 20°C kg/m3 | 7,700 | |
|---|---|---|
| Modulus of Elasticity kN/mm2 at | 20°C | 220 |
| 200°C | 210 | |
| 400°C | 195 | |
| 500°C | - | |
| Thermal Conductivity W/m K at 20°C | 25 | |
| Specific Thermal Capacity at 20°C J/kg K | 460 | |
| Electrical Resistivity at 20°C Ω mm2 /m | 0.60 | |
Shipping:
Quality inspection:
Application
About us:
workshop:
service:
FAQ:
Q:Can you make the product according to our requirements?
A: Yes, we will strictly follow your requirements, such as the way of the package, the length of the product, the treatment of the product and so on.
Q:What is your way of the surface treatment?
A:We can paint oil as your requirement on the product.
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.