ASTM AISI 316LN S31653 Stainless Steel Sheet DIN1.4429 ESR Metal Sheet 0.5-10mm

ASTM AISI 316LN S31653 Stainless Steel Sheet DIN1.4429 ESR Metal Sheet 0.5-10mm

Type 316LN stainless steel is austenitic steel suitable for the fabrication of many products. Due to its molybdenum content, it can be used in applications that require increased corrosion resistance.

It has a more stable austenitic structure, which means it provides a lower magnetic permeability. The nitrogen content adds additional resistance to sensitization.

Similar to types 316 and 316L stainless steel, type 316LN provides great resistance to general corrosion and pitting/crevice corrosion.

Common Names:

• Stainless steel type 316N is commonly known as Chromium-Nickel steel.

Executive Standards/Grades:

• JIS: G4303
• ASTM: ASTM A240, ASTM A213, ASTM A276 and so on.
• DIN: 1.4406
• UNS: S31653
• EN: X2CrNiMoN17-13-3
• SUS: SUS316LN

Chemical Properties:

Type 316LN stainless steel has the following chemical composition:

• Carbon – 0.03%
• Manganese – 2.00%
• Chromium – 16.0% – 18.0%
• Nickel – 10.0% – 14.0%
• Molybdenum – 2.0% – 3.0%
• Sulphur – 0.03%
• Phosphorus – 0.045%
• Silicon – 1.00%
• Nitrogen – 0.10 – 0.30%
• Iron – Balance

Mechanical Properties:

• Hardness (HRB) – 95 (maximum)
• Elongation (%) – 60
• Yield Strength (Mpa) – 205
• Tensile Strength (Mpa) – 515
• Poisson’s Ratio – 0.27 – 0.30

Physical Properties:

• Density (8000 Kg/M3)
• Elastic Modulus (Gpa) – 200
• Thermal Conductivity (Btu/ft hr ⁰ F) – 8.4 – 16.3
• Specific Heat (Btu/lb/°F) – 0.116 at 200 oF
• Electrical Resistivity (µohm/cm) – 7.4

Key Features:

• Low-carbon, nitrogen-enhanced version of Type 316, providing higher resistance to sensitization
• Its nitrogen content provides solid solution hardening, increasing the minimum specified yield strength
• Excellent resistance to oxidation and low rate of scaling at temperatures up to 1650oF
• Provides more resistance to atmospheric and other types of corrosion
• Is considered one of the most weldable of the stainless steels
• Hot forming can be performed in the range of 1560 – 2100 oF
• Type 316LN can be formed and fabricated by any cold forming operation

Forms Available:

Stainless steel type 316LN is available in different forms such as:

• Sheet
• Seamless
• Coiled
• Rod coil
• Plate

Stainless steel features:

1. Complete product specifications and diverse materials;
2. High dimensional accuracy, up to ±0.1mm;
3. Excellent surface quality, good brightness;
4. Strong corrosion resistance, high tensile strength and fatigue strength;
5. Stable chemical composition, pure steel, low inclusion content;
6. The package is in good condition and the price is favorable;
7. Can be done without calibration.