EN 10088-2-2005 1.4418 X4CrNiMo16-5-1 Martensitic Stainless Steel Round Bar OD 250mm
Price:
3.15 USD/KG
MOQ:
50KG
Delivery Time:
7 Days
Brand:
TSING SHAN
Product Description
EN 10088-2-2005 1.4418 X4CrNiMo16-5-1 Martensitic Stainless Steel Round Bar OD 250mm
| Grade : | X4CrNiMo16-5-1 | ||||||||
| Number: | 1.4418 | ||||||||
| Classification: | Martensitic stainless steel | ||||||||
| Density: | 7.7 g/cm ³ | ||||||||
| Standard: |
|
||||||||
| Equivalent grades: | 1.4418 |
Chemical composition % of steel X4CrNiMo16-5-1 (1.4418): EN 10088-2-2005
| Tighter carbon ranges may be agreed at the time of enquery and order Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended. Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. |
| C | Si | Mn | Ni | P | S | Cr | Mo | N |
| max 0.06 | max 0.7 | max 1.5 | 4 - 6 | max 0.04 | max 0.015 | 15 - 17 | 0.8 - 1.5 | max 0.02 |
Mechanical properties of steel X4CrNiMo16-5-1 (1.4418)
| Rm - Tensile strength (MPa) (+QT) | 760-1100 |
| Rm - Tensile strength (MPa) (+A) | 1100 |
| Rp0.2 0.2% proof strength (MPa) (+QT) | 550-700 |
| KV - Impact energy (J) (+QT) | +20° 55-90 |
-20° 40 |
| A - Min. elongation at fracture (%) longitud., (+QT) | 16 |
| A - Min. elongation at fracture (%) transverse, (+QT) | 14 |
| Brinell hardness (HB): (+A) | 320 |
Equivalent grades of steel X4CrNiMo16-5-1 (1.4418)
| EU EN |
France AFNOR |
Sweden SS |
||
| X4CrNiMo16-5-1 |
|
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben