Hot Rolled Bright Surface High Strength 17-4PH Stainless Steel Round Bar
Price:
1.87
MOQ:
50
Delivery Time:
Negotiable
Product Description
630 Stainless Steel Properties 630 Round Bar
17-4PH Stainless Steel Overview
17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. This alloy maintains high strength up to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium/columbium additions. This grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized through heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
This grade should not be used at temperatures above 572°F (300°C) or at very low temperatures. It provides adequate resistance to atmospheric corrosion and diluted acids or salts, with corrosion resistance equivalent to Alloy 304 or 430.
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Corrosion Resistance
Alloy 17-4 PH withstands corrosive attacks better than standard hardenable stainless steels and is comparable to Alloy 304 in most media. For stress corrosion cracking risks, higher aging temperatures above 1022°F (550°C), preferably 1094°F (590°C), should be selected.
1022°F (550°C) is the optimum tempering temperature in chloride media, while 1094°F (590°C) is optimal for H2S media. The alloy may experience crevice or pitting attack if exposed to stagnant seawater for extended periods. It provides corrosion resistance in chemical, petroleum, paper, dairy, and food processing industries equivalent to 304L grade.
Technical Specifications
Chemical Composition
Table 1: Composition ranges for grade 630 stainless steels
| Element | Content (%) |
|---|---|
| C | 0.07 max |
| Mn | 1.0 max |
| Si | 1.0 max |
| P | 0.04 max |
| S | 0.030 max |
| Cr | 15.0 - 17.5 |
| Ni | 3.0 - 5.0 |
| Cu | 3.0 - 5.0 |
| Nb+Ta | 0.15 - 0.45 |
Mechanical Properties
Table 2: Mechanical properties of grade 630 stainless steels
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HRC) | Hardness Brinell (HB) |
|---|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max | 363 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
Physical Properties
Table 3: Typical physical properties of grade 630 stainless steels
| Property | Value |
|---|---|
| Density (kg/m³) | 7750 |
| Mean Coefficient of Thermal Expansion 0-100°C (µm/m/°C) | 10.8 |
| Mean Coefficient of Thermal Expansion 0-315°C (µm/m/°C) | 11.6 |
| Thermal Conductivity at 100°C (W/m·K) | 18.4 |
| Thermal Conductivity at 500°C (W/m·K) | 22.7 |
| Specific Heat 0-100°C (J/kg·K) | 460 |
| Electrical Resistivity (nΩ·m) | 800 |
Applications
- Engine components
- High strength boat propeller shafts
- Plastic moulding dies
- Valves and gears
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben