ASTM A564 H1075 Heat Treated 630 Stainless Steel Round Bar with Corrosion Resistance
Price:
1.87
MOQ:
50
Delivery Time:
Negotiable
Product Description
630 Stainless Steel Bar ASTM A564 Type 630 H1075 Round Bar
17-4PH Stainless Steel Overview
17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. This alloy maintains high strength up to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. This grade combines high strength, hardness (up to 572°F/300°C), and excellent corrosion resistance. Mechanical properties can be optimized through heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Corrosion Resistance
Alloy 17-4 PH provides superior corrosion resistance compared to standard hardenable stainless steels and is comparable to Alloy 304 in most media. For stress corrosion cracking prevention, higher aging temperatures above 1022°F (550°C) are recommended. The alloy offers excellent corrosion resistance in chemical, petroleum, paper, dairy, and food processing industries.
Chemical Composition
Table 1: Composition ranges for grade 630 stainless steels
| Element | Content (%) |
|---|---|
| C | 0.07 max |
| Mn | 1.0 max |
| Si | 1.0 max |
| P | 0.04 max |
| S | 0.030 max |
| Cr | 15.0 - 17.5 |
| Ni | 3.0 - 5.0 |
| Cu | 3.0 - 5.0 |
| Nb+Ta | 0.15 - 0.45 |
Mechanical Properties
Table 2: Mechanical properties of grade 630 stainless steels
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HRC) | Hardness Brinell (HB) |
|---|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max | 363 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
Heat Treatment
Grade 630 stainless steels undergo solution treatment at 1040°C for 0.5 hours followed by air cooling. Age hardening at low temperatures achieves required mechanical properties with minimal distortion.
Table 6: Typical mechanical properties after solution treating
| Condition | Hardening Temp (°C) | Time (h) | Typical Hardness Rockwell C | Tensile Strength (MPa) |
|---|---|---|---|---|
| A | Ann | - | 36 | 1100 |
| H900 | 482 | 1 | 44 | - |
| H925 | 496 | 4 | 42 | 1170-1320 |
| H1025 | 552 | 4 | 38 | 1070-1220 |
| H1075 | 580 | 4 | 36 | 1000-1150 |
| H1100 | 593 | 4 | 35 | 970-1120 |
| H1150 | 621 | 4 | 33 | 930-1080 |
Applications
- Engine components
- High strength boat propeller shafts
- Plastic moulding dies
- Valves and gears
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben