Type 630 (17-4PH) Stainless Steel Round Bar
17-4 Precipitation Hardening (Type 630/UNS S17400) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. This alloy maintains high strength up to approximately 600°F (316°C).
Material Overview
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. This grade combines high strength, hardness (up to 572°F/300°C), and corrosion resistance. Mechanical properties can be optimized through heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Corrosion Resistance
Alloy 17-4 PH withstands corrosive attacks better than standard hardenable stainless steels and is comparable to Alloy 304 in most media. For stress corrosion cracking prevention, higher aging temperatures above 1022°F (550°C) are recommended. The alloy provides corrosion resistance in chemical, petroleum, paper, dairy, and food processing industries equivalent to 304L grade.
Chemical Composition
| Element | Content (%) |
|---|---|
| C | ≤ 0.07 |
| Mn | ≤ 1.00 |
| Si | ≤ 1.00 |
| P | ≤ 0.04 |
| S | ≤ 0.030 |
| Cr | 15.0 - 17.5 |
| Ni | 3.0 - 5.0 |
| Cu | 3.0 - 5.0 |
| Nb+Ta | 0.15 - 0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C |
|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min |
Physical Properties
| Property | Value |
|---|---|
| Density | 7750 kg/m³ |
| Thermal Expansion (0-100°C) | 10.8 µm/m/°C |
| Thermal Conductivity (100°C) | 18.4 W/m·K |
| Specific Heat (0-100°C) | 460 J/kg·K |
| Electrical Resistivity | 800 nΩ·m |
Heat Treatment
Solution treatment involves heating to 1040°C for 0.5 hours followed by air cooling. Age hardening at various temperatures achieves specific mechanical properties:
| Condition | Hardening Temp (°C) | Time (h) | Typical Hardness (HRC) | Tensile Strength (MPa) |
|---|---|---|---|---|
| A | Ann | - | 36 | 1100 |
| H900 | 482 | 1 | 44 | - |
| H925 | 496 | 4 | 42 | 1170-1320 |
| H1150 | 621 | 4 | 33 | 930-1080 |
Fabrication & Applications
Grade 630 can be welded using conventional methods without pre-heating and machined in solution-treated condition. Primary applications include:
- Engine components
- High-strength boat propeller shafts
- Plastic molding dies
- Valves and gears
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben