Hot Rolled 17-4PH Stainless Steel Round Bar with Bright Surface and OD 6-300mm
Price:
3.19
MOQ:
50
Delivery Time:
Negotiable
Product Description
17-4PH Stainless Steel Round Rod / Stainless Steel Bar
High-strength precipitation hardening stainless steel with excellent corrosion resistance and mechanical properties.
Product Specifications
| Product | 17-4PH Stainless Steel Round Bar |
|---|---|
| Standard | ASTM GB DIN EN |
| Diameter | 8 - 450mm |
| Length | 6m /pcs or cutting as requested |
| Finishing | Black Bar / Bright Bar |
| Main Grades | 201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276, C4, C22, Inconel 600, 625, Incoloy 800, 825, 825H, etc. |
| Service | Cutting, surface polishing, heat treatment |
| Brand | Walsin, BAOSTEEL, TISCO, QINGSHAN |
Material Description
17-4 Precipitation Hardening (Type 630) is a chromium-copper precipitation hardening stainless steel used for applications requiring high strength and moderate corrosion resistance. High strength is maintained to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with Cu and Nb/Cb additions. The grade combines high strength, hardness (up to 572°F / 300°C), and corrosion resistance. Mechanical properties can be optimized with heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
The grade should not be used at temperatures above 572°F (300°C) or at very low temperatures. It has adequate resistance to atmospheric corrosion or in diluted acids or salts where its corrosion resistance is equivalent to Alloy 304 or 430.
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Chemical Composition
Composition of 17-4PH Stainless Steel (Grade 630):
| Element | Min | Max |
|---|---|---|
| C | - | 0.07 |
| Mn | - | 1.00 |
| Si | - | 1.00 |
| P | - | 0.04 |
| S | - | 0.030 |
| Cr | 15.00 | 17.50 |
| Ni | 3.00 | 5.00 |
| Cu | 3.00 | 5.00 |
| Nb+Ta | 0.15 | 0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C (HR C) | Hardness Brinell (HB) |
|---|---|---|---|---|---|
| Solution Treated | 1105 typ | 1000 typ | 15 typ | 38 max | 363 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min | 388 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min | 277 min |
Physical Properties
| Property | Value |
|---|---|
| Density (kg/m³) | 7750 |
| Thermal Conductivity at 100°C (W/m.K) | 18.4 |
| Thermal Conductivity at 500°C (W/m.K) | 22.7 |
| Specific Heat 0-100°C (J/kg.K) | 460 |
| Electrical Resistivity (nΩ.m) | 800 |
| Mean Coefficient of Thermal Expansion 0-100°C (µm/m/°C) | 10.8 |
| Mean Coefficient of Thermal Expansion 0-315°C (µm/m/°C) | 11.6 |
Product Images
Applications
- Engine components
- High strength and boat propeller shafts
- Plastic moulding dies
- Valves and gears
Contact Us
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben