Cold Rolled Grade 321 Stainless Steel Round Bar with Bright Surface for High Temperature Applications
Price:
2.59
MOQ:
50
Delivery Time:
Negotiable
Product Description
Diameter 6-250mm Stainless Steel Round Rod / Black Stainless Steel Bar Grade 321 After Solid Solution
Product Specifications
| Products | Stainless Steel Round Bar |
|---|---|
| Grade | 321 / 1.4541 / UNS S32100 |
| Standard | ASTM A276/276M |
| Diameter | 8 - 300mm |
| Length | 6m/pcs or cutting any length as requested |
| Surface | Black, Bright |
| Other Grades | 304, 310S, 316L, 317L, 321, 410, 420, 431, 440A/B/C, 2205, 2507, 630, 631, 904L, etc. |
| Service | Cutting, Polishing, Heat Treatment |
Stainless Steel Bar Product Range
| Products Name | Size Range | Mainly Grade |
|---|---|---|
| Stainless Steel Round Bar (hot rolled black surface) | 8 - 300mm | 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 321, 347, 410, 420, 431, 440A/B/C, 2205, 2507, 904L, 254SMO, 17-4PH, 17-7PH, etc. |
| Stainless Steel Round Bar (bright polished) | 3 - 50mm | 201, 304, 316L, 310S, 2205, 630, etc. |
| Stainless Steel Square Bar | 4×4 - 50×50mm | 201, 304, 316L, 310S, 410, 420, etc. |
| Stainless Steel Hexagon Bar | S4-S70 | 201, 304, 316L, 310S, 410, 420, etc. |
| Stainless Steel Flat Bar | 10×3 - 100×40 | 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 321, 347, 410, 420, 431, 440A/B/C, 2205, 2507, 904L, 254SMO, 17-4PH, 17-7PH, etc. |
| Stainless Steel Angle Bar | 30×30 - 200×200 | 201, 304, 316L, 310S, 2205, etc. |
| Stainless Steel Channel Bar | 50×25 - 200×100 | 201, 304, 316L, 310S, 2205, etc. |
About 321 Stainless Steel
Alloy 321 (UNS S32100) is a titanium-stabilized stainless steel that offers excellent resistance to intergranular corrosion following exposure to temperatures in the chromium carbide precipitation range from 800 to 1500°F (427 to 816°C). The addition of titanium stabilizes the alloy against chromium carbide formation.
Alloy 321 stainless steel provides superior mechanical properties for high-temperature service, offering higher creep and stress rupture properties than Alloy 304 and particularly Alloy 304L. It resists oxidation up to 1500°F (816°C) and maintains good low-temperature toughness.
Alloy 321H (UNS S32109) is the higher carbon (0.04-0.10) version developed for enhanced creep resistance and higher strength at temperatures above 1000°F (537°C). In most instances, the carbon content enables dual certification.
Alloy 321 stainless steel cannot be hardened by heat treatment, only by cold working. It can be easily welded and processed using standard shop fabrication practices.
Chemical Composition of 321 Stainless Steel
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Other |
|---|---|---|---|---|---|---|---|---|---|---|
| 321 | - 0.08 |
2.00 | 0.75 | 0.045 | 0.030 | 17.0-19.0 | - | 9.0-12.0 | 0.10 | Ti=5(C+N) 0.70 |
| 321H | 0.04-0.10 | 2.00 | 0.75 | 0.045 | 0.030 | 17.0-19.0 | - | 9.0-12.0 | - | Ti=4(C+N) 0.70 |
| 347 | 0.08 | 2.00 | 0.75 | 0.045 | 0.030 | 17.0-19.0 | - | 9.0-13.0 | - | Nb=10(C+N) 1.0 |
Mechanical Properties of 321 Stainless Steel
| Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50 mm) min | Rockwell B (HR B) max | Brinell (HB) max |
|---|---|---|---|---|---|
| 321 | 515 | 205 | 40 | 95 | 217 |
| 321H | 515 | 205 | 40 | 95 | 217 |
| 347 | 515 | 205 | 40 | 92 | 201 |
Applications of 321 Stainless Steel
- Aircraft exhaust manifolds
- Expansion joints
- Bellows
- Furnace parts
- Heating element tubing
- Heat exchangers
- Woven or welded screens for high-temperature mineral processing
- Spiral welded tube for burner pipes and flues
Product Images
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben