Product Description
Diameter 3-50mm Stainless Steel Bar Grade 17-4PH / 630
High-performance precipitation hardening stainless steel rods offering exceptional strength and corrosion resistance for demanding industrial applications.
Diameter Range: 3-50mm
Material Grade: 17-4PH / 630
Standards: ASTM, GB, DIN, EN
Available Length: 6m standard or custom cutting
Product Specifications
| Product | 17-4PH Stainless Steel Round Bar |
|---|---|
| Diameter Range | 8-450mm |
| Length | 6m per piece or custom cutting available |
| Finishing | Black Bar / Bright Bar |
| Available Grades | 201, 301, 303Cu, 304, 304L, 309S, 310S, 316L, 316Ti, 317L, 318, 321, 347, 410, 420, 430, 431, 440a/b/c, 904L, 2205, 2507, Hastelloy C276/C4/C22, Inconel 600/625, Incoloy 800/825/825H |
| Services | Cutting, surface polishing, heat treatment |
| Brands | Walsin, BAOSTEEL, TISCO, QINGSHAN |
Material Description
17-4PH Stainless Steel (Type 630) is a chromium-copper precipitation hardening stainless steel designed for applications requiring high strength and moderate corrosion resistance. This grade maintains high strength up to approximately 600°F (316°C).
General Properties
Alloy 17-4 PH is a precipitation hardening martensitic stainless steel with copper and niobium additions. It combines high strength, hardness (up to 572°F / 300°C), and excellent corrosion resistance. Mechanical properties can be optimized through heat treatment, achieving very high yield strength up to 1100-1300 MPa (160-190 ksi).
Applications & Standards
| Applications | Standards |
|---|---|
|
|
Chemical Composition
| Element | Content (%) |
|---|---|
| Carbon (C) | ≤ 0.07 |
| Manganese (Mn) | ≤ 1.00 |
| Silicon (Si) | ≤ 1.00 |
| Phosphorus (P) | ≤ 0.04 |
| Sulfur (S) | ≤ 0.030 |
| Chromium (Cr) | 15.0 - 17.5 |
| Nickel (Ni) | 3.0 - 5.0 |
| Copper (Cu) | 3.0 - 5.0 |
| Niobium + Tantalum (Nb+Ta) | 0.15 - 0.45 |
Mechanical Properties
| Condition | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell C |
|---|---|---|---|---|
| Solution Treated | 1105 (typical) | 1000 (typical) | 15 (typical) | 38 max |
| Condition 900 | 1310 min | 1170 min | 10 min | 40 min |
| Condition 1150 | 930 min | 724 min | 16 min | 28 min |
Physical Properties
| Property | Value |
|---|---|
| Density | 7750 kg/m³ |
| Thermal Conductivity at 100°C | 18.4 W/m·K |
| Thermal Conductivity at 500°C | 22.7 W/m·K |
| Specific Heat (0-100°C) | 460 J/kg·K |
| Electrical Resistivity | 800 nΩ·m |
Heat Treatment
Solution Treatment (Condition A): Heated at 1040°C for 0.5 hours, then air-cooled to 30°C. Small sections may be oil quenched.
Hardening: Age-hardened at low temperatures to achieve required mechanical properties. During processing, superficial discoloration occurs with shrinkage of 0.10% for condition H1150 and 0.05% for condition H900.
Product Images
Applications
- Engine components
- High-strength boat propeller shafts
- Plastic molding dies
- Valves and gears
- Aerospace components
- Nuclear industry equipment
Contact Information
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben