ASTM A240 Hot Rolled S23043 S32304 Duplex Stainless Steel Plate with High Yield Strength and Corrosion Resistance
Price:
2.25
MOQ:
50
Delivery Time:
Negotiable
Product Description
ASTM A240 Hot Rolled S23043 S32304 1.4362 Stainless Steel Plate
Alloy 2304 (UNS S32304) is a 23% chromium, 4% nickel, molybdenum-free duplex stainless steel with corrosion resistance properties similar to 316L. Its mechanical properties, including yield strength, are approximately twice those of 304L/316L austenitic grades, enabling weight savings in properly designed pressure vessel applications.
Chemical Composition
Typical Values (Weight %)
| Carbon | Chromium | Nickel | Molybdenum | Nitrogen | Others |
|---|---|---|---|---|---|
| 0.020 | 23 | 4 | 0.2 | 0.1 | S=0.001 |
PREN = [Cr%] + 3.3 [Mo%] + 16 [N%] ≥ 24
Mechanical Properties
Tensile Properties (Minimum Values)
| °C | Rp 0.2 MPa | Rp 1.0 MPa | UTS MPa | °F | YS 0.2% Offset KSI | YS 0.1% Offset KSI | UTS KSI | Elongation % |
|---|---|---|---|---|---|---|---|---|
| 20 | 400 | 440 | 600 | 68 | 58 | 64 | 87 | 25 |
| 100 | 330 | 365 | 570 | 212 | 48 | 53 | 83 | 25 |
| 200 | 280 | 310 | 530 | 392 | 41 | 45 | 77 | 20 |
| 300 | 230 | 260 | 490 | 572 | 33 | 38 | 71 | 20 |
Values obtained for hot rolled plates (th ≤ 2"). Alloy 2304 must not be used for extended periods at temperatures above 300°C (572°F) due to precipitation hardening.
Toughness Values (KCV Minimum Values)
| Temperature | Single | Average (5) |
|---|---|---|
| -50°C / -60°F | 75 J/cm² / 54 ft.lbs | 90 J/cm² / 65 ft.lbs |
| +20°C / +70°F | 90 J/cm² / 65 ft.lbs | 150 J/cm² / 87 ft.lbs |
Hardness (Typical Values)
HV10: 180-230 | HB: 180-230 | HRC: ≤20
Physical Properties
Density: 7,800 kg/m³ (0.28 lb/in³)
| Temperature Interval °C | Thermal Expansion α×10⁻⁶K⁻¹ | Resistivity (μΩ·cm) | Thermal Conductivity (W·m⁻¹·K⁻¹) | Specific Heat (J·kg⁻¹·K⁻¹) | Young Modulus E (GPa) | Shear Modulus G (GPa) |
|---|---|---|---|---|---|---|
| 20-100 | 13 | 80 | 17 | 450 | 200 | 75 |
| 20-100 | 13 | 92 | 18 | 500 | 190 | 73 |
| 20-200 | 13.5 | 100 | 19 | 530 | 180 | 70 |
| 20-300 | 14 | 105 | 20 | 560 | 170 | 67 |
Microstructure
The chemical composition of 2304 is optimized to achieve a typical 50% austenite / 50% ferrite microstructure after solution annealing at 950°-1050°C (1742°-1922°F). The microstructure exhibits greater stability compared to molybdenum-containing duplex stainless steels, with intermetallic phases appearing only after 10 hours in the 750°-850°C (1382°-1562°F) range.
Processing Guidelines
Hot Forming
Perform hot forming in the 1150°-900°C (2100°-1650°F) range. Post-forming solution annealing at 950°-1050°C (2100°-1650°F) is recommended to restore corrosion resistance and mechanical properties. Proper support during heating is essential to prevent creep deformation.
Cold Forming
Alloy 2304 can be cold formed using standard 304L/316L equipment. Higher stresses are required due to increased yield strength. Final solution annealing after cold forming restores mechanical and corrosion resistance properties.
Descaling
Use standard 304L/316L solutions and pastes. Pickling times are longer than for austenitic grades due to the alloy's superior corrosion resistance.
Machinability
Alloy 2304 duplex offers improved machinability, particularly in drilling operations, with performance equivalent to 316LEZ. Enhanced corrosion resistance and cleanliness are achieved without sulfur additions, improving localized corrosion resistance.
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben