Heat Resistant 253MA Stainless Steel Plate Hot Rolled with Polished Surface S30815
Price:
3.65
MOQ:
100
Delivery Time:
Negotiable
Product Description
Heat Resistant Plate Inox 253mA Stainless Steel Plate UNS S31805
UNS S30815 253MA stainless steel plate is a specialized grade that combines excellent high-temperature service properties with ease of fabrication. This material resists oxidation at temperatures up to 1150°C and provides superior performance to Grade 310 in carbon, nitrogen, and sulphur-containing atmospheres.
Also known by the proprietary designation 2111HTR, 253MA contains relatively low nickel content, offering advantages in reducing sulphide atmospheres compared to high nickel alloys and Grade 310. The inclusion of high silicon, nitrogen, and cerium contents provides excellent oxide stability, high elevated temperature strength, and superior resistance to sigma phase precipitation. The austenitic structure ensures excellent toughness, even at cryogenic temperatures.
Specifications and Standards
ASME SA 182, ASME SA 213, ASTM A 240, ASTM A 276, ASTM A 312, ASTM A 479, UNS S30815, Werkstoff 1.4835
Common Stainless Steel Grade Specifications
| ASTM | JIS | AISI | EN |
|---|---|---|---|
| S30100 | SUS301 | 301 | 1.431 |
| S30400 | SUS304 | 304 | 1.4301 |
| S30403 | - | 304L | 1.4307 |
| S31008 | SUS310S | 310S | 1.4845 |
| S31603 | - | 316L | 1.4404 |
| S32100 | SUS321 | 321 | 1.4541 |
| S41008 | SUS410S | 410S | - |
| S43000 | SUS430 | 430 | 1.4016 |
| S43932 | - | - | 1.451 |
| S44400 | SUS444 | 444 | 1.4521 |
| S44500 | SUS430J1L | - | - |
Dimension Ranges
Width: 600mm - 2030mm
Thickness: 0.1mm - 120.0mm
Length: 300mm - 6000mm, Maximum 18000mm
Thickness: 0.1mm - 120.0mm
Length: 300mm - 6000mm, Maximum 18000mm
Surface Finish: No.1, 2B, BA, No.3, No.4, No.5, No.8, HL, Etching, SB, Ti-coating, color-coating, embossing
Applications
- Furnace components including burners, retorts, conveyor belts, fans, jigs and baskets, rollers, walking beams, radiant tubes, electric heater elements, refractory anchors, hoods, flues, grates, expansion bellows
- Petrochemical and refinery tube hangers
Equivalent Materials
ASTM A182 Grade FXM-19, ASTM A269 Grade TPXM-19, ASTM A580 Grade S20910, ASTM A193 Grade B8R Class 1C, ASTM A276 Grade S20910, ASTM A813 Grade TPXM-19, ASTM A193 Grade B8R Class 1D, ASTM A312 Grade TPXM-19, ASTM A814 Grade TPXM-19, ASTM A193 Grade B8RA Class 1C, ASTM A314 Grade S20910, ASTM A943 Grade TPXM-19, ASTM A194 Grade 8R, ASTM A336 Grade FXM-19, ASTM A959 Grade S20910, ASTM A194 Grade 8RA, ASTM A358 Grade A240 XM-19, ASTM A965 Grade FXM-19, ASTM A213 Grade XM-19, ASTM A403 Grade CRXM-19, AISI XM-19, ASTM A240 Grade S20910, ASTM A403 Grade WPXM-19, SAE XM-19, ASTM A249 Grade TPXM-19, ASTM A479 Grade S20910, UNS S20910
Chemical Composition
| Element | Min (%) | Max (%) |
|---|---|---|
| C | 0.05 | 0.10 |
| Mn | - | 0.80 |
| Si | 1.10 | 2.00 |
| P | - | 0.040 |
| S | - | 0.030 |
| Cr | 20.0 | 22.0 |
| Ni | 10.0 | 12.0 |
| N | 0.14 | 0.20 |
| Ce | 0.03 | 0.08 |
Mechanical Properties
| Property | Value |
|---|---|
| Tensile Strength (MPa) min | 600 |
| Yield Strength 0.2% Proof (MPa) min | 310 |
| Elongation (% in 50mm) min | 40 |
| Rockwell B (HR B) max | 95 |
| Brinell (HB) max | 217 |
Physical Properties
| Property | Value |
|---|---|
| Density (kg/m³) | 7800 |
| Elastic Modulus (GPa) | 200 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-100°C | 17.0 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-600°C | 18.5 |
| Mean Coefficient of Thermal Expansion (mm/m/°C) 0-1000°C | 19.5 |
| Thermal Conductivity (W/m.K) at 20°C | 15.0 |
| Thermal Conductivity (W/m.K) at 1000°C | 29.0 |
| Specific Heat 0-100°C (J/kg.K) | 500 |
| Electrical Resistivity (nW.m) | 850 |
International Grade Comparisons
| UNS No | Euronorm No | Euronorm Name | Swedish SS | Japanese JIS |
|---|---|---|---|---|
| S30815 | 1.4835 | X9CrNiSiNCe21-11-2 | 2368 | - |
Note: These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed, original specifications must be consulted.
Possible Alternative Grades
| Grade | Why it might be chosen instead of 253MA |
|---|---|
| 310 | Carburising atmospheres require a higher nickel content |
| 304H | Lower cost alternative, provided the operating temperature is below about 800°C |
| Nickel Alloys | Carburising atmospheres or temperatures above the 1100 - 1150°C maximum of 253MA |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
TSING SHAN STEEL INDUSTRIAL LIMITED
Location
NO.288,Youyi Road Xi Shan Dristrict , Wuxi, Jiangsu, China
Contact Person
Gao Ben