High Viscosity Modified Phenolic Resin Epoxy HW-650M Amine Hardener For Epoxy
Epoxy hardener HW-650M is a modified phenolic amine epoxy curing agent mainly produced with cardanol. It is a general curing agent for epoxy anticorrosion system with high viscosity, environmentally friendly solvent free, good film forming and excellent comprehensive performance.
Performance:
Environmental-friendly solvent free, high viscosity;
Good film formation, excellent comprehensive performance, good general matching;
Excellent adhesion, flexibility, impact resistance and other mechanical properties.
1. The physical and chemical properties
| Test Item | Technical Data | Test Method |
| Appearance | Orange clear liquid | Visual method |
| Viscosity (mPa·s,25℃) | 20000-50000 | GB/T 2794-2013 |
| Amine value (mg KOH/g) | 270-300 | CS 113 |
| Color (Gardner) | ≤15 | GB/T 22295-2008 |
| Solid content (%) | solvent free | GB/T 1725-2007 |
| A.H.E.W. | 174 | Theoretical calculation |
| Paint film 25℃(dry time Hr) | 7 | GB 1728-2020 |
| Gelling time 25℃(min) | 40-100 | GB 12007.7-89 |
| E51: curing agent=100: (90±5) E44: curing agent=100: (75±5) E20: curing agent=100: (35±5) | ||
2. Application
It is widely used in industrial anti-corrosion coatings, floor coatings, adhesives, and other fields, such as steel structures, ships, pipelines, storage tanks, etc.
The most suitable working environment: temperature 5 ℃-35 ℃, humidity ≤ 85%.
3. Storage and transportation
Ventilated cool place, shelf life of one year.
Non-dangerous goods can be transported as general goods.
Regular 200kg iron drum packing or according to customer's specific requirements for packaging.
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.