High Adhesion Hot Melt Resin Middle Temperature Transparent

Price Negotiable

Price: Negotiable

MOQ: Negotiable

Delivery Time: Negotiable

Brand: PLG

Product Description

Grade:VF790

Product: Hot Melt Adhesive Resin For Aluminum Plastic Panel And Heat Insulation Panel

Advantages

Good film forming performance, can be formed into 0.02 ㎜ thick film;
High adhesive strength, good durability, excellent adhesive interface performance, showing the interface adhesive cohesion energy destruction;
Can withstand a certain acid, alkali, salt spray and other chemical solvent corrosion;
Strong adaptability, can meet the needs of high-speed production;
Good weather resistance, adapt to the climate temperature change environment, can be outdoor use.

Descriptions

VF790 is a maleic anhydride and vinyl acetate functionalized polyethylene mixture, easy to form film, with excellent processability and adhesive strength.

Physical Properties

Properties	Standard	Test Condition	Units	Typical Value
Density	ASTM D1505	23℃	g/cm3	0.93
MFR	ASTM D1238	230℃,2.16 kg	g/10min	1.8
Shore Hardness	ASTM D2240	Shore D	—	45

Mechanical Properties

Properties	Standard	Test Condition	Units	Typical Value
Tensile Yield Strength	ASTM D638	100mm/min	Mpa	6.2
Tensile Breaking Strength	ASTM D638	100mm/min	Mpa	13.7
Elongation at Break	ASTM D638	100mm/min	%	＞750

Thermal Properties

Properties	Standard	Test Condition	Units	Typical Value
Melting Point	ASTM D3418	10℃/min	℃	105
VSP	ASTM D1525	2℃/min	℃	80

Note:The datas is used for referential purpose only, not for quality commitment.

Chemical Structure

Composition: Maleic Anhydride and Vinyl Acetate functionalized polyethylene mixture.

Application

VF790 is widely used as binder for aluminum plastic panel and heat insulation panel.

Statement: the above processing technology shall be different according to different conditions such as product size, mold design and processing equipment specification, and the details shall be adjusted according to the actual situation.