Q235 A36 Carbon Structural Steel Plate 1095 Alloy Carbon Steel Plates Sheets
Hot Sales Carbon Steel Plate Q235 A36 1095 Alloy Carbon Steel Plates Sheets
|
ASTM A285 is a type of ordinary carbon steel intended for fusion-welded pressure vessel equipments as boiler, storage tank, heat exchangers, etc. With 3 steel grades (Grade A, Grade B, Grade C) covering tensile strength range from 310-515Mpa,usually ASTM A285 steel plate is delivered as-rolled condition. made by killed, semi-killed, capped or rimmed steel practices according to the end users’ requirement. it has good weld-ability for fusion weld need for pressure vessel equipment, its max thickness is limited to 50mm in order to insure its mechanical property. We could supply hot rolled and cold rolled ASTM A285 steel plate, customers can also have specific fabrication cutting ( any size and any shape ) drilling, welding, milling, machining and steel structure according to drawing. |
Product Paramenters
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) | ||||||
| C | Mn | Ni | Cr | Mo | Ti | |||
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 | |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
|
Y.S (N/MM2) |
T.S (N/MM2) |
EL (%) |
HRB |
Specific Heat (J/g℃) |
Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.
316Ti: Mainly used for industrial components.
|