Single Crystal NMC622 Cathode Powder LiNi0.6Co0.2Mn0.2O2 with High Discharge Capacity and Low Impurity Content for Lithium Battery Research

Single crystal NMC622 S76L (LiNi_0.6Co_0.2Mn_0.2O₂) is a high-performance single crystal ternary cathode material engineered for advanced lithium battery research and manufacturing applications.

• Fe: 0.0015 wt%
• Cu: 0.0005 wt%
• Ca: 0.0035 wt%
• Na: 0.0188 wt%
• Zn: 0.0002 wt%

• Tapped Density: 2.10 g/cm³
• Apparent Density: 0.91 g/cm³
• Specific Surface Area: 0.74 m²/g
• Particle Size: D10=2.56μm, D50=5.14μm, D90=10.02μm
• Spherical single crystal particles without impurity crystal phase
• Black uniform powder verified by XRD & SEM analysis

• 100 cycles: 98% capacity retention
• 200 cycles: 96.5% capacity retention
• 300 cycles: 94% capacity retention
• Excellent high & room temperature storage performance
• Low inflation rate during cycling

Compatible with both artificial graphite and natural graphite systems.

• Active Material: 94.5%
• Super P: 2%
• KS6: 1%
• HSV900: 2.5%

• Suggested Compaction Density: 3.50-3.55 g/cm³
• Maximum Compaction: ≥3.60 g/cm³

• Academic electrochemistry experiments
• Electrode formula development
• Prismatic/coin cell prototype testing
• High-capacity lithium battery mass production

Each production batch includes comprehensive material characterization with XRD, SEM, PSD analysis, and complete electrical cycle test reports.