9229V Flame Retardant Epoxy Resin Liquid Epoxy Based Resin Compound
Production details:
Formulation:
| Epoxy resin | LE- 9229V | 100pbw |
| Hardener | LH-9229V | 100pbw |
| Filling | Silica flour (SIO2) | 280-340pbw |
| Color paste | LC-series * | 3pbw |
| Process parameter | APG | Vacuum process |
| Mix temperature | 40℃/1-2 hours | 60℃/1-2hours |
| Feeding process | Pressure(0.5-5bar) | Vacuum |
| Mold temperature | 130-150℃ | 80-100℃ |
| Gelation times | 30-60min | 3-6hours |
| Cure conditions | 130-140℃×6-10hours | 130-140℃×6-10 hours |
| LE- 9229V is a kind of modified BPA epoxy resin | |||
| Properties | Standard | Unit | Value |
| Appearance | Visual | Milky white viscous liquid | |
| Viscosity at 25℃ | ISO12058 | mPa.s | 10.5-16.5 |
| Density at 25℃ | ISO1675 | g/cm3 | 1.16--1.20 |
| Vapor pressure | (Knudsen) | Pa | ﹤0.01 |
| Flash point | ISO1523 | ℃ | About 135 |
| Properties | Standard | Value | Properties | Standard | Value |
| Tg.(DSC) | ISO11357-2 | 105-125℃ | Thermal conductivity | ISO11357-2 | 0.8-0.9W/mk |
| Tensile strength | ISO527 | 65-95N/ mm2 | Thermal degradation temperature | ISO527 | ＞320℃ |
| Flexural strength | ISO178 | 110-150N/ mm2 | Water absorption(23℃×10days) | ISO178 | 0.10-0.20 %by wt. |
| Compressive strength - | ISO604 | 130-190N/ mm2 | Water absorption (100℃×60 mins) | ISO604 | 0.08-0.15 %by wt. |
| Impact strength | ISO179 | 11-18kJ/ m2 | Surface resistivity | ISO179 | 1014Ω |
| Cure shrinkage | ISO178 | 0.7-0.9% | Volume resistivity | ISO178 | 1015Ω.cm |
| Flammability(4mm) | ISO1210 | HB | Dielectric strength | ISO1210 | 30 kv/mm |
| Flammability(12mm) | V0 | Loss factor | 0.02 |
Storage:
The components have to be stored in tightly sealed and dry original containers in an environment at 6~35°C;. Under these conditions, the shelf life will correspond to the expiration date stated on the label ( normally 12 months). After this date, the product may be reanalyzed to confirm if it validates yet. Partial emptied containers should be closed tightly immediately after use.
Packaging:
Company profile:
Shanghai Wenyou Industry Co., Ltd. is a professional epoxy resin company located in Shanghai, China, established in 2008. Specializing in the manufacturing, R&D, and sales of epoxy resin, curing agents, and related products.
Our wide range of products includes epoxy resin, flame retardant resin, curing agents, outdoor modifiers, toughening agents, epoxy paste, demoulding agents, and fillers.
We have obtained ISO9001, ISO14001, SGS, and UL certifications, and our products comply with ROHS and REACH safety regulations.
Our high-quality products are used in high voltage electrical insulation applications and are exported globally. We are committed to providing stable products and excellent service to the global electricity industry.
Applications:
Electrical Insulation: Epoxy electrical resins exhibit excellent electrical insulation properties, effectively preventing current leakage and short circuits. Therefore, they are widely used in the manufacture of electrical equipment and components such as insulators, transformers, cable insulation layers, and printed circuit boards. They provide reliable electrical insulation, protecting electronic devices from electric shocks and electrical failures.
Exhibition:
Our advantages:
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.