30 Mils LDPE LLDPE PVC HDPE Geomembrana For Dam Pond Liner Landfill Mining
Price:
Negotiation
MOQ:
1000 Square Meter
Delivery Time:
7 -20days
Brand:
Geomax
Product Description
PRODUCT DESCRIPTION
Smooth Textured HDPE LDPE LLDPE PVC Geomembrane For Dam Pond Liner Landfill Mining
Product Introduction
Construction Method
1. The slope shall be laid in order from top to bottom. Don't pull it too tight.
2. Tow adjacent longitudinal joints should not be in a horizontal line, should bestaggered more than 1m each other.
3. Longitudinal joints should be more than 1.50m away from the dam foot and bending foot, and should be located on the plane.
4. When the slope is laid, the direction of spreading film should be basically parallel to the slope line.
5. The construction, first of all to use small diameter sand or clay levelingbase, and then laid the geomembrane. The geomembrane should not be stretched too tight, and the part of the soil bured at both ends is corrugated. A transitional layer of about 10cm is laid on the geomembrane with sand or clay.
2. Tow adjacent longitudinal joints should not be in a horizontal line, should bestaggered more than 1m each other.
3. Longitudinal joints should be more than 1.50m away from the dam foot and bending foot, and should be located on the plane.
4. When the slope is laid, the direction of spreading film should be basically parallel to the slope line.
5. The construction, first of all to use small diameter sand or clay levelingbase, and then laid the geomembrane. The geomembrane should not be stretched too tight, and the part of the soil bured at both ends is corrugated. A transitional layer of about 10cm is laid on the geomembrane with sand or clay.
Specifications
| Specification | Test method | Unit | Type | ||||
| thickness | ASTM 05199 | mm | 0.75 | 1 | 1.25 | 1.5 | 2 |
| density | ASTM 0 1505 | g/cm3. min. | 0.939 | 0.939 | 0.939 | 0.939 | 0.939 |
| tensile strength at yield | ASTM 06693 | KN/m. min. | 11 | 15 | 18 | 22 | 29 |
| tensile strength at break | ASTM 06693 | KN/m. min. | 20 | 27 | 33 | 40 | 53 |
| elongation at yield | ASTM 06693 | %.max. | 12 | 12 | 12 | 12 | 12 |
| elongation at break | ASTM 06693 | %.max. | 700 | 700 | 700 | 700 | 700 |
| tear resistance | ASTM 0 1004 | N | 93 | 125 | 156 | 187 | 249 |
| puncture resistance | ASTM 04833 | N | 240 | 320 | 400 | 480 | 640 |
| environment stress cracking resistance | ASTM 05397 | hr | 300 | 300 | 300 | 300 | 300 |
| carbon black content | ASTM 0 1603 | % | 2-3 | 2-3 | 2-3 | 2-3 | 2-3 |
| oxidation induction time (OIT) | ASTM 03895 | minute | 100 | 100 | 100 | 100 | 100 |
| low temperature (-70'C)impact brittle |
ASTM 02136 | pass | pass | pass | pass | pass | |
| stream hydraulic conductivity | g.cm/(cm².s.Pa), max. |
1x10¯13 | 1x10¯13 | 1x10¯13 | 1x10¯13 | 1x10¯13 | |
| dimension stability after 2 storge 1 h/100'C | ASTM 0 1204 | %.max | 2 | 2 | 2 | 2 | 2 |
HCNS Manufacture
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Anhui Hechuang New Synthetic Materials Co., Ltd
Location
1602, Building 11th, Mingfa Center, Hefei City, Anhui Province,China
Contact Person
Xu