FKM Rubber Precompound FD Series, 20-60 Mooney Viscosity, 17 Compression Set
Founded in 2002, headquartered in Chengdu National Industrial Park - Meishan Jinxiang Industrial Park.
- The largest FKM manufacturer in China, with actual output of 5500mt in 2022
- 2 CNAS approved labs
- 1 10,000 clarification workshop for smart-wearable devices
- 1 100,000 clarification workshop for FKM precompounds and compounds
- 13 producing lines for FKM precompounds and compounds
FD-601E is a wide molecular weight distribution fluoroelastomer precompound which includes copolymer of hexa-fluoropropylene and vinylidene-fluoride, curatives. It is designed for compression molding products such as O-ring, V-ring and gasket.
| F Content | 66% |
| Specific Gravity | 1.81 |
| Physical form | Slab |
| Color | Off-white |
| Solubility | Ketones and Esters |
| Mooney Viscosity ML 1+10@ 121ºC | 61 |
- Excellent low temperature resistance
- Excellent chemical resistance
- Good mold flow
- Low compression set
FD-601E can be compounded with internal mixers or two-roll mills with standard fillers and other ingredients that are used in typical fluoroelastomer formulations. All the dry ingredients should be blended before adding to the rubbery solid. During compounding, full cooling should be accompanied. After mixing, the compound should be cooled as quickly as possible.
FD-601E is packed with PE film in carton. The weight is 20kg net per carton.
- Store in well ventilated place
- Smoking is forbidden strictly in working areas
- Avoid eye contact
- Wash thoroughly any contacted skin and clothing after handling
For further safety and handling guidance, please follow the product's Material Safety Data Sheet or consult Dowhon's people.
| Compound | phr |
|---|---|
| FD-601E | 100 |
| N990 | 30 |
| MgO-150 | 3 |
| Ca(OH)2 | 6 |
| Carnauba Wax | 1 |
GOTECH Moving Die Rheometer (GT-M3000A) 100 cpm 0.5 Arc 177ºC@ 6min
| Value | Test Method | |
|---|---|---|
| ML, lb.in | 2.21 | ASTM D6601 |
| MH, lb.in | 21.36 | ASTM D6601 |
| Ts2, min | 1:08 | ASTM D6601 |
| T10, min | 1:07 | ASTM D6601 |
| T90, min | 2:16 | ASTM D6601 |
Press Cure 180ºC@5min, Post Cure 230ºC@24hour
| Value | Test Method | |
|---|---|---|
| Tensile Strength, Mpa | 15.9 | ASTM D412 |
| Elongation at Break, % | 210 | ASTM D412 |
| Hardness, Shore A | 75 | ASTM D412 |
| 200ºC@70h | 18 | ASTM D395, method B |
| Tr10, ºC | -17 | ASTM 1329 |
20kgs/25kgs per carton by courier (FedEx, DHL etc); 500kgs/625kgs/700kgs per pallet for shipping.
ISO9001, ISO14001, IS016949
Currently has 65 patents, 15 invention patents are under application, participated in the formulation of 4 National Standards.
BY air MOQ is 20-25KG, by sea MOQ is 100KG.
For stock goods, we can arrange delivery within 3 working days, otherwise delivery time is around 7-14 working days.
Usually goods are packaged with PE film in carton. The weight is 20-25kg net per carton. 500kgs/625kgs/700kgs in a pallet.
Please contact our sales, we'll recommend suitable grade according to your typical physical properties and other related information.