Electrical Insulation Battery Pack Wrap Battery Wrapping Silicone Rubber Film
Price:
Fuzhou Fuqiang Precision Co.,Ltd.
MOQ:
Customized
Delivery Time:
1000 pcs/ days
Brand:
FQ
Product Description
Battery Wrapping Flame Hardness Shore A Barrier Films High Flame Retardant Silicone Rubber Battery Thermal Wrap
Main Features
It is used to realize buffering energy absorption between battery pack cells.
-
Refractory silicone rubber composite layer of ultra-high strength stubborn fabric makes it have high mechanical strength;
-
It can maintain solid structural integrity at high temperatures or flame, and has excellent electrical insulation;
-
Low smoke, low flame and low smoke toxicity during combustion;
- It can be processed to ultra-thin thicknesses and has excellent flexibility.
Specification
The main performance parameters are shown in Table
| Serial number | Test items | Unit | Test Standard | SR No. | |||
| SR 35-A | SR 40-A | SR 50-A | SR 60-A | ||||
| 1 | Hardness | Shore A | GB/T531.1-2008 | 35±7 | 40±10 | 50±10 | 60±10 |
| 2 | Density | g/cm3 | 4.3.2 | 0.8≤μ±3σ≤1.4 | 1.00≤μ±3σ≤1.51 | 1.00≤μ±3σ≤1.51 | 1.1≤μ±3σ≤1.5 |
| 3 | 25℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.25≤μ±3σ≤0.75 | 10%: 0.45≤μ±3σ≤0.80 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.63≤μ±3σ≤1.77 | 20%: 0.95≤μ±3σ≤1.45 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.20≤μ±3σ≤2.24 | 30%: 1.50≤μ±3σ≤2.50 | ||||
| 4 | 25℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 5 | 25℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 6 | -30℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.08≤μ±3σ≤.0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.35≤μ±3σ≤0.65 | 10%:0.55≤μ±3σ≤0.90 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.90≤μ±3σ≤1.20 | 20%:1.10≤μ±3σ≤1.95 | ||||
| 30%:0.45≤μ±3σ≤0.9 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.50≤μ±3σ≤2.00 | 30%: 2.00≤μ±3σ≤3.95 | ||||
| 7 | -30℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 8 | -30℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 9 | 60℃ Compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%:0.35≤μ±3σ≤0.70 | 10%: 0.35≤μ±3σ≤0.80 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%:0.80≤μ±3σ≤1.30 | 20%:0.65≤μ±3σ≤1.60 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%:1.00≤μ±3σ≤2.10 | 30%: 1.00≤μ±3σ≤2.50 | ||||
| 10 | 60℃ Shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 11 | 60℃ Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 12 | Double 85 post-aging compression curve | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%: 0.50≤μ±3σ≤0.70 | 10%: 0.40≤μ±3σ≤1.90 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%: 0.90≤μ±3σ≤1.30 | 20%: 1.00≤μ±3σ≤3.20 | ||||
| 30%:0.45≤μ±3σ≤0.75 | 30%:0.68≤μ±3σ≤1.32 | 30%: 1.40≤μ±3σ≤2.10 | 30%: 1.70≤μ±3σ≤5.50 | ||||
| 13 | Double 85 post-aging shear performance under pressure | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 | ||
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 14 | Double 85 post-ageing Tensile strength | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 15 | Compression curve after high and low-temperature cycle | MPa | GB/T 7757-2009 | 10%:0.12≤μ±3σ≤0.22 | 10%:0.25≤μ±3σ≤0.53 | 10%: 0.45≤μ±3σ≤0.65 | 10%: 0.50≤μ±3σ≤2.20 |
| 20%:0.25≤μ±3σ≤0.45 | 20%:0.50≤μ±3σ≤0.86 | 20%: 0.85≤μ±3σ≤1.35 | 20%: 1.00≤μ±3σ≤4.00 | ||||
| 30%:0.45≤μ±3σ≤0.7 | 30%:0.68≤μ±3σ≤1.32 | 30%: 1.30≤μ±3σ≤2.50 | 30%: 1.80≤μ±3σ≤6.80 | ||||
| 16 | Shear performance under pressure after high and low temperature | MPa | ASTM C273C /273M-16 | Strength: µ-3σ≥0.8 | Shear strength under pressure: µ-3σ≥0.5 | Shear strength under pressure: µ-3σ≥0.2 | Shear strength under pressure: µ-3σ≥0.8 |
| Modulus: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | Shear modulus under pressure: Min≥0.75 | ||||
| 17 | Tensile strength after high and low-temperature cycle | MPa | GB/T 528-2009 | µ-3σ≥0.8 | µ-3σ≥1.1 | µ-3σ≥1.65 | / |
| 18 | Flame retardant | / | UL94 | UL94 V0(2mm) | V0(t≥2mm) | V0(t≥2mm) | V0(t≥2mm) |
| V1(1≤t＜2mm) | V1(1≤t＜2mm) | V1(1≤t＜2mm) | |||||
| HB(0.4≤t＜1mm) | HB(0.4≤t＜1mm) | HB(0.4≤t＜1mm) | |||||
| 19 | Forbidden object | / | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV | RoHS &REACH & ELV |
| 20 | Insulation | MΩ | 1000V DC 60s | µ-3σ≥500 | µ-3σ≥500 | µ-3σ≥500 | µ-3σ≥500 |
| 21 | Impedance | mA | 2700V DC 60s | µ+3σ≤1 | µ+3σ≤1 | µ+3σ≤1 | µ+3σ≤1 |
| 22 | Thermal conductivity | W/(m·K) | GB/T 10295-2008 | µ+3σ≤0.8 | µ+3σ≤0.8 | µ+3σ≤0.8 | µ+3σ≤0.8 |
| 23 | Specific heat capacity | J/(g·K) | ASTM E1269-2011 | µ-3σ≥0.9 | µ-3σ≥0.9 | µ-3σ≥0.9 | µ-3σ≥0.9 |
| 24 | Stress retention rate | % | GB/T1685-2008 | ≥40 | ≥40 | ≥40 | ≥40 |
| 25 | 25℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.8 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 26 | -30℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 27 | 60℃ Shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥0.6 | Min≥1.5 |
| 28 | Double 85 ageing shear strength with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
| 29 | Shear strength after high and low-temperature cycles with double-sided adhesive | MPa | ASTM D1002 | Min≥0.6 | Min≥0.8 | Min≥1.1 | Min≥1.5 |
Applications of Silicone Rubber Gasket Sheet
60 Shore A durometer silicone rubber gasket sheets are appropriate for use as aircraft gaskets. We provide gaskets using materials that meet Boeing and Airbus FAR specifications where required. Our silicone gasket sheet range also includes:
Industries
• Agriculture and Livestock• Mining and Quarrying
• Mineral Processing
• Power Generation
• Construction
• Oil and Gas
Package & Delivery
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Fuzhou Fuqiang Precision Co., Ltd.
Location
No. 188, Wuchen Road, Dongtai Industrial Park, Qingkou Town, Minhou County
Contact Person
Fuqiang