Product Description
Manifold Hydraulic Valve Block Hydraulic Motor Cushion Valve For Rotary Excavator
The design of hydraulic valve block is mostly non-standard design, which needs to be conducted according to different working conditions and use requirements
The design of valve block is divided into the following steps: material selection, design, processing and heat treatment, deburring and
Cleaning, surface anti-rust treatment and test.
Different materials determine different pressure levels. First, select materials reasonably according to the service pressure. Generally
The following principles shall be followed:
When the working pressure P<6.3MPa, the hydraulic valve block can be cast iron HT20-40. Cast iron can be used
In order to carry out mass casting, reduce working hours and improve efficiency, especially suitable for standardized valve blocks.
When 6.3MPa ≤ P<21MPa, the hydraulic valve block can be aluminum alloy forgings, No. 20 forged steel or Q235;
Low carbon steel has good welding performance, especially suitable for non-standard hard pipes (many valve blocks need to be welded with hard pipes in use
Connect).
When P ≥ 21MPa, the hydraulic valve block can be made of 35 # forged steel. Direct machining or machining after forging
Post quenching and tempering HB200-240 (general high-pressure valve blocks are often subject to flaw detection, machining and heat treatment cycles.
The design of valve block is divided into the following steps: material selection, design, processing and heat treatment, deburring and
Cleaning, surface anti-rust treatment and test.
Different materials determine different pressure levels. First, select materials reasonably according to the service pressure. Generally
The following principles shall be followed:
When the working pressure P<6.3MPa, the hydraulic valve block can be cast iron HT20-40. Cast iron can be used
In order to carry out mass casting, reduce working hours and improve efficiency, especially suitable for standardized valve blocks.
When 6.3MPa ≤ P<21MPa, the hydraulic valve block can be aluminum alloy forgings, No. 20 forged steel or Q235;
Low carbon steel has good welding performance, especially suitable for non-standard hard pipes (many valve blocks need to be welded with hard pipes in use
Connect).
When P ≥ 21MPa, the hydraulic valve block can be made of 35 # forged steel. Direct machining or machining after forging
Post quenching and tempering HB200-240 (general high-pressure valve blocks are often subject to flaw detection, machining and heat treatment cycles.
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Dongguan Zhongwei Metal Products Co., Ltd
Location
Dongguan, China
Contact Person
Gong