NON DG Isocyanate And Polyol For Air Filter Low Odor
Polyol and Isocynate for the air filter
JYLQ－01A/B
Introduction:
JYLQ-01A is made up of polymer polyol, grafted polyether polyol, cross linker, blowing agent, and composite catalyst. JYLQ-01B is made up of modified MDI. This system has good liquidity with easy
process. This system is applied to produce the air filter for the car or other industry facility.
Typical Properties
| Item Unit | JYLQ-01A | JYLQ-01B | |
|
Appearance NCO Viscosity(25℃)Density (20℃) Storage temp. Shelf life |
% mpa.s g/ml ℃ Months |
Milky white liquid / 1200±300 1.05±0.05 15－25 12 |
Brown liquid 29.4±1 100±30 1.20±0.05 15－25 12 |
- ＊Under the recommending temperature, keeping in the original dry barrels of storage; B-side is suggested using nitrogen seal save as much as possible after opening.
Recommended ratio
| Weight ratio | |
|
JYLQ-01A JYLQ-01B |
100 30-40 |
REACTIVE PROPERTY (Material temperature is 25℃)
| By hand | Machine | ||
|
Cream time (s) Gel time (s) Mold temperature (℃) Demould time (min)FRD (kg/m3) |
s s ℃ min kg/m3 |
55-60 70-80 35-55 8-10 350-400 |
9-10 65-75 35-55 8-10 350-400 |
TYPICAL PHYSICAL PROPERTY
| Unit | Data | |
|
Moulded density Tensile strength Elongation (%) Tear strength Hardness |
Kg/m3 Kpa % N/cm Shore A
|
400 ≥80 ≥130 ≥3.2 25-45 |
- The above technical data are tested by our own, is not subject to any restriction in law.
The final interpretation of this specification is owned by our company.