Stable Blend Polyols 90 percent closed cell foam provide Dimensional stability without blowing agent cyclopentane which should be added by technical guidance
Stable Blend Polyols 90 percent closed cell foam provide Dimensional stability without blowing agent cyclopentane which should be added by technical guidance
Product Introduction
JYP-103N is made from Rigid Polyether Polyol, Polyester Polyol, silicone oil, catalyst, some other additives.
After adding some percentage blowing agent cyclopentane, JYP-103M can be reacted with MDI for making sandwich panels.
The finished products enjoy good mixing property, stable foaming, excellent fluidity and flat surface.
The foam produced by the combination of polyether and polymeric MDI has better thermal insulation performance and low temperature dimensional stability.
Typical physical properties
| Property | JYP-103N | Standard |
|
Appearance Viscosity(25C) ,mpa ·s Density(20C) ,g/ml OHV ,mgKOH/g Water content ,(%) |
yellow transparent liquid 2000-4000 1.12- 1. 17 220-360 1.0-3.0 |
/ GB/T 12008.7-2010 GB/T 15223-2008 GB/T 12008.3-2009 GB/T 22313-2008 |
Package
220kg net per steel drum；1000kg per IBC drum
Shelf Life
12 months in original drum, should be kept in the cool and dry place.