95% Ceramic Powder Granulation A Al2o3 Alumina Ceramic Powder
Ceramic granulation grain 95 % ceramic firing molding ceramic raw materials alumina ceramic powders
Product name : Alumina granulation powder
Specification : HY-ZLF-95
Shape : White particles
Process : rapid dry pressing, static pressure, hot die casting, spraying
Features : low temperature ceramic parts, high density, powder does not stick to the mold, no cracking, no pores after ceramic, powder consistency is good.
Type : Alumina ceramics, toughening ceramics, wear-resistant ceramics, talc ceramics, porcelain powder.
performance index
| index | unit | 95% ceramics |
| AL2O3 | % | ≥95 |
| AL2O3 grain diameter | μm | 0.8 |
| density | ≥g/m³ | 1.06~1.1 |
| mcisture | % | 0.3 |
| particle size distribution | μm | 60~250 |
| Porcelain density | ≥g/m³ | ≥3.7 |
| average shrinkage ratio | % | 16.5-17.5 |
| burning temperature | ℃ | ≤1620 |
| ignition loss | % | ＜5 |
| Porcelain color | slight yellow,white |
In the production process of alumina ceramics, in the process of dry pressing or isostatic pressing, it is necessary to form a granular powder by spray drying of the ceramic slurry. It is required to have good fluidity and certain strength of the particles. In the process of transportation and feeding, it is not broken, and there is a certain particle level ratio. When feeding, it is closely packed, has certain bonding characteristics and lubrication characteristics, and should not be bonded to each other.