Alkali Resistance Alumina Silica Fire Brick Custom Silica Refractory Brick For Glass Furnace
Price:
200-800 USD
MOQ:
1 Ton
Delivery Time:
10-20 Days
Brand:
Rongsheng Xinwei
Product Description
Factory Price Silica Refractory Brick Alumina Silica Fire Brick Custom Silica Bricks For Glass Furnace
Description of Factory Price Silica Refractory Brick
The main components are tridymite, cristobalite and a small amount of residual quartz, acidic refractory materials in glass phase.The silica content is above 94%. The true density is 2.35g/cm3. It has the performance of resisting acid slag corrosion. Higher high temperature strength. The initial temperature of softening under load is 1620~1670℃. Long-term use under high temperature without deformation. Low thermal shock stability (heat exchange in water is 1 to 4 times). Natural silica is used as raw material, and an appropriate amount of mineralizer is added to promote the conversion of quartz into tridymite in the green body. Fire slowly at 1350~1430°C under reducing atmosphere. When heated to 1450°C, a total volume expansion of 1.5~2.2% will occur, and this residual expansion will make the cuts tightly bonded together to ensure good air tightness and structural strength of the masonry.
20 Years experience in refractories, Stable Capability, High Quality, Professional Refractory Technical Team, Provide Free Sample For Testing, Excellent Service, Competitive Price is the most important advantage of our products.
Features Alumina Silica Fire Brick
1. Excellent chemical attack resistance, slag resistance and acid resistance;
2. No pollution to products (such as molten glass, etc.); The main component of silicon brick is SiO2, and if there are blocks or surface droplets during use, the quality of molten glass will not be affected.
3. Excellent thermal stability, the product will not explode during hot repair, and the repair operation can be carried out directly;
4. High temperature volume stability, no shrink in burn repeatedly.
5. Small bulk density. The mass of the furnace can be reduced.
6. After repair (hot repair), there will be no peeling and other phenomena, and it is safe and reliable for long-term use;
Applications of Alumina Silica Fire Brick
Silica bricks are mainly used for the partition walls of the carbonization chamber and combustion chamber of coke ovens, the regenerative chamber of steel making open hearth furnaces, soaking pits, refractory materials of glass furnaces, Tunnel kilns, rotary kilns, metallurgical furnaces,and ceramic firing kilns, as well as other load-bearing parts of kilns. It is also used for high-temperature load-bearing parts of hot air furnaces and acidic open hearth furnaces.
Silica bricks are also widely used in construction and equipment in chemical, petroleum, pharmaceutical and other industries.
Product Paramenters Of Alumina Silica Fire Brick For Glass Furnace
|
Item
|
Silica brick
for coke oven
|
Silica brick
for glass kiln
|
||||
|
Furnace bed
|
others
|
BG-96A
|
BG-96B
|
BG-95A
|
BG-95B
|
|
|
SiO2% ≥
|
94
|
96
|
96
|
95
|
95
|
|
|
Fe2O3 %≥
|
/
|
0.8
|
1.0
|
1.2
|
1.2
|
|
|
0.2MPa RUL°C ≥
|
1650
|
1680
|
1670
|
1660
|
1650
|
|
|
FUSION INDES:
one BRICK<20kg one BRICK ≥20kg |
/
/ |
0.5
0.6 |
/
/ |
0.7
0.7 |
/
/ |
|
|
True density g/cm3 ≤
|
2.34
|
2.35
|
2.34
|
|||
|
PLC % 1450°C×2h
|
+0.2
|
0
|
/
|
|||
|
AP % ≤
|
22(23)
|
24
|
22(24)
|
|||
|
Thermal expansion
1000°C % ≤ |
1.28
|
1.30
|
/
|
|||
|
CCS MPa ≥
one brick<20kg one brick≥20kg |
30
|
25
|
35(30)
30(25) |
|||
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Henan Rongsheng Xinwei New Materials Research Institute Co., Ltd
Location
11th Floors, Building 6, China Central Electronic Commerce Port, Daxue Road, Zhengzhou, Henan, China
Contact Person
Jacky Han