20μm Thickness Clear PET Non Silicone Coated Release Film for Electronics and Medical Applications
Price:
Negotiable
MOQ:
30000 s.q.m.
Delivery Time:
within 45 days, depends on the reserve of raw materials
Brand:
HSF
Product Description
20μm Clear PET Non Silicone Coated Release Film
This clear PET non-silicone coated release film is designed for demanding applications in electronics, medical, automotive, and printing industries. Made from clear polyester (PET) with a non-silicon release agent coating on one side, it provides reliable performance without silicone transfer contamination.
Key Applications
- Labels & Stickers: Used as backing material for labels, stickers, and decals, allowing easy separation and application
- Medical Devices: Serves as liner for wound dressings and transdermal patches, maintaining sterility without contamination
- Packaging Materials: Functions as release liner for pouches and bags, providing visibility while protecting against moisture
- Electronic Components: Used with adhesive tapes and protective films, preventing damage during release processes
- Graphic Overlays & Membrane Switches: Provides protective layer during manufacturing with optical clarity for electronic devices
- Surface Protection & Masking: Safeguards glass, metal, and plastic surfaces during handling and fabrication processes
Technical Advantages
- Eliminates silicon transfer contamination issues
- Compatible with silicone and gel applications
- Cost-effective alternative to fluorine-coated films
- Transparent design allows for visual inspection and alignment
Technical Specifications
| Test Item | Unit | Value | Test Method |
|---|---|---|---|
| Thickness | μm | 19.46 | DIN53370 |
| Color | - | Transparent | - |
| Tensile Strength MD | N/mm² | 182 | DIN53455-6-5 |
| Tensile Strength TD | N/mm² | 216 | DIN53455-6-5 |
| F-5 MD | N/mm² | 97.8 | DIN53455-6-5 |
| F-5 TD | N/mm² | 89.4 | DIN53455-6-5 |
| Elongation @ Break MD | % | 116 | DIN53455-6-5 |
| Elongation @ Break TD | % | 96 | DIN53455-6-5 |
| Elasticity Modulus MD | N/mm² | 3565 | DIN53455-6-5 |
| Elasticity Modulus TD | N/mm² | 3840 | DIN53455-6-5 |
| Friction Coefficient F/M-US | - | 0.411 | DIN53375 |
| Friction Coefficient F/M-UK | - | 0.315 | DIN53375 |
| Haze | % | 70.6 | ASTM D1003 |
| Luminousness | % | 75.8 | ASTM D1003 |
| Glossiness | % | 26.5-28 | ASTM D2457 |
| Thermal Shrinkage MD | % | 1.5 | ASTM D1204 150℃, 30min |
| Thermal Shrinkage TD | % | 0 | ASTM D1204 150℃, 30min |
| Wetting Tension | mN/m | 58 | ASTM D2578 |
| Release Force | gf/25mm | 3 | Final 10, 20hrs |
| Sub-sequent Adhesion Rate | % | 87% | - |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Shanghai HSF Materials Technology Co., Ltd.
Location
Area D, No. 218 North Huting Road, Songjiang District, 201600 Shanghai, China
Contact Person
Bryan J. Lee