60μm Red-Black Dual-Color Cast Polypropylene Film with 25μm Emboss Depth for High Tensile Strength and Tear Resistance
Price:
Negotiable
MOQ:
2000kg
Delivery Time:
15 working days
Brand:
HSF
Product Description
60μm CPP Red-Black Dual-Color Embossed Film
This premium cast polypropylene film features a distinctive red-black dual-color design with precise 25μm emboss depth, offering exceptional visual appeal and functional performance for packaging applications.
Production Process
Manufactured using advanced cast extrusion and precision embossing technology. High-purity CPP resin is melted in temperature-controlled extruders (160-180℃), then co-extruded with red and black masterbatches to create a dual-color base film with consistent 60μm thickness. The material undergoes precision embossing to achieve 25μm uniform emboss depth, followed by trimming, tension control, and winding into defect-free rolls.
Key Features
- 60μm base thickness with 25μm uniform emboss depth
- Vivid red-black dual-color co-extrusion with excellent color fastness
- Smooth, even embossed surface with superior scratch resistance
- Balanced tensile strength and tear resistance with good flexibility
- Compatible with lamination and heat-sealing processes
- Optional food-grade certification available
Product Advantages
The 60μm base thickness provides optimal balance between flexibility and durability, while the 25μm emboss depth enhances texture and anti-slip performance. The distinctive red-black dual-color design offers unique aesthetic appeal for packaging applications. Excellent batch-to-batch consistency in color, thickness, and emboss pattern minimizes production waste. Non-toxic, odorless, and easy to process, this film combines practicality with visual appeal for cost-effective mass production.
Application Environment
Widely used in food packaging, gift packaging, cosmetic packaging, and industrial packaging applications. Performs reliably in dry, normal-temperature environments (0℃ to 60℃) and moderate storage conditions. Suitable for high-speed slitting, lamination, heat-sealing, and printing processes. Ideal for customers seeking both aesthetic appeal and practical performance in packaging materials.
Product Specifications
| Test Item | Unit | Industry Standard Requirement | Product Specified Standard | Actual Test Result | Qualification Judgment |
|---|---|---|---|---|---|
| Base Film Thickness (excl. emboss) | μm | 60±5 | 60±3 | 59.6 | Qualified |
| Emboss Depth | μm | 25±3 (customizable) | 25±2 | 24.9 | Qualified |
| Tensile Strength (MD/TD) | MPa | ≥16/≥14 | ≥18/≥16 | 19.3/17.2 | Qualified |
| Elongation at Break (MD/TD) | % | ≥260/≥210 | ≥280/≥230 | 292/245 | Qualified |
| Heat Seal Strength (120℃, 0.3MPa, 1s) | N/15mm | ≥8 | ≥10 | 11.5 | Qualified |
| Surface Tension (corona treated side) | mN/m | ≥38 | ≥40 | 40.8 | Qualified |
| Tear Resistance (MD/TD) | N | ≥13/≥10 | ≥14/≥11 | 15.2/12.4 | Qualified |
| Moisture Barrier Property (23℃, 85%RH) | g/(m²·24h) | ≤6.0 | ≤5.5 | 5.2 | Qualified |
| Oil Resistance (soaked in n-hexane for 24h) | - | No obvious swelling, discoloration | No swelling, discoloration, adhesion | No swelling, discoloration, adhesion | Qualified |
| Hardness (Shore D) | HD | 51±5 | 51±3 | 50.9 | Qualified |
| Emboss Adhesion | - | No texture peeling by tape test | No texture peeling, color fading by 3M tape test | No texture peeling, color fading by 3M tape test | Qualified |
| Weather Resistance (UV aging for 72h) | - | No obvious fading, cracking | Fading grade ≤2, no cracking, deformation | Fading grade 1, no cracking, deformation | Qualified |
| Environmental Performance (food contact grade) | - | Compliant with GB 4806.7-2016 | Compliant with GB 4806.7-2016, no peculiar smell, no harmful precipitation | Compliant with GB 4806.7-2016, no peculiar smell, no harmful precipitation | Qualified |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.