Radiation Cross-Linked Heat Shrink Tape for Pipeline Weld Joint Corrosion Protection
Price:
US$10.00-30.00
MOQ:
100 Pieces
Delivery Time:
30DAYS
Brand:
huashida
Product Description
Product Description
Radiation Cross-Linked Heat Shrink Tape for Pipeline Weld Joint Corrosion Protection
![Radiation Cross-Linked Heat Shrink Shrinkable Tape for Welding Joint Field-Applied Pipeline]()
Heat shrinkable sleeve/belt developed and manufactured by Qingdao Huashida Machinery Co., Ltd for anti-corrosion of pipeline, is composed by radiation cross-linked polyethylene backing and adhesive (2 layers).
During connecting pipes, the hot melt adhesive is squeezed into the joint by the shrink power to form a perfectly sealed surface after being heated. It has good performance in pipeline waterproof, anti-chemical corrosion, insulation and anti-aging.
Application area:
It is mainly used for wrapping around the pipe, anti-corrosion of kinds of pipe joints, and repairing pipes.
For example Oil and gas pipe, PU insulation pipe, 3PE/2PE steel pipe.
Feature of our heat shrinkable sleeve:
1.Fast shrinkage speed,
2.good waterproof performance,
3 good anti-corrosive performance,
4.long service life, convenient transportation and fast construction.
5.using pure PE material and imported adhesive for ensuring the quality
TECHNICAL PARAMETERS
| NO | Test Item | Unit | Performance | Test Result | Test Method | ||
| Back Material | |||||||
| 1 | Tensile Strength | MPa | ≥17 | 19.47 | ASTM D638 | ||
| 2 | Elongation | % | ≥400 | 626 | ASTM D638 | ||
| 3 | Vicat Softening Point | ºC | ≥90 | 92 | ASTM D1525 | ||
| 4 | Brittleness Temperature | ºC | <-65 | <-65 | ASTM D2671C | ||
| 5 | Dielectric Strength | MV/m | ≥25 | 33.13 | ASTM D149 | ||
| 6 | Volume Resistivity | Ω.m | ≥1*1013 | 1.1*1013 | ASTM D257 | ||
| 7 | Environment Stress Crack | h | ≥1000 | >1000 | GB/T1842 | ||
| 8 |
Chemical resistance (7d) |
10% HCI |
Tensile strength | MPa | ≥85 | 104.9 | ASTM D638 |
| Elongation | % | ≥85 | 96.3 | ASTM D638 | |||
| 10% Naah |
Tensile strength | MPa | ≥85 | 102.1 | ASTM D638 | ||
| Elongation | % | ≥85 | 95.6 | ASTM D638 | |||
| 10% NaCl |
Tensile strength | MPa | ≥85 | 108.3 | ASTM D638 | ||
| Elongation | % | ≥85 | 94.1 | ASTM D638 | |||
| 9 | Thermal aging (150ºC,168h) |
Tensile strength | MPa | ≥14 | 20.7 | ASTM D638 | |
| Elongation | % | ≥300 | 630 | ASTM D638 | |||
| NO. | Test Item | Unit | Performance | Text Result | Text Method | |
| Adhesive | ||||||
| 1 | Softening Point | ºC | ≥90 | 90.1 | ASTM E28 | |
| 2 | Brittleness Temperature | ºC | <-15 | <-15 | ASTM D2671C | |
| 3 | Lap Shear | MPa | ≥1.0 | 1.5 | ASTM D1002 | |
| 4 |
Peel Strength (23±2ºC) |
Steel | N/cm | ≥70 | 145.6 | ASTM D1000 |
| Primer | N/cm | ≥70 | 205.9 | ASTM D1000 | ||
| PE layer | N/cm | ≥70 | 190.0 | ASTM D1000 | ||
| Non-solvent Epoxy Primer | ||||||
| 5 | Shear of cured primer | MPa | ≥5.0 | 12 | SY/T0041 | |
Heat shrinkable sleeve for Oil & Gas Pipe
Heat shrinkable sleeve for Thermo Insulated Pipe
For metal reinforced HDPE corrugated pipe (drainpipe)
DELIVERY
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Qingdao Huashida Machinery Co., Ltd.
Location
69 Jinsheng Second Road Chengyang District, Qingdao, Shandong, China
Contact Person
yuki