98A Hot Melt Adhesive Low Temperature Lamination Solution Hot Melt TPU for Chemical Hot Melt Sheet and Fire Hose Co-Extrusion with Good Initial Strength For Clothes
98A Hot Melt Adhesive Low Temperature Lamination Solution Hot Melt TPU for Chemical Hot Melt Sheet and Fire Hose Co-Extrusion with Good Initial Strength For Clothes
Production Process:
Mold: Solvent processing, Injection molding, Extrusion molding, Calender
Drying requirements: Please dry at 90-100℃ for 3-4 hours;
Injection temperature: 190-195 degrees for the first section, 195-200 degrees for the second section, and 195-210 degrees for the third section
Features:
Excellent physical properties,
Good initial strength & solvent solubility,
Fast crystallization,
Low temperature lamination
Technical Datasheet:
| Content | Hardness | 100%Modulus | 300%Modulus | Ring and Ball Softening Point | Tear strength | Tensile Strength | Breaking Elongation |
| Test Method | ISO R 868 | ASTM D-412 | ASTM D-412 | ASTM D3461 | ASTM D-624 | ASTM D-412 | ASTM D-412 |
| Test units | ShoreA/D | mpa | mpa | ℃ | N/mm | Mpa | % |
| DHMA-98A-1 | 98A | 8 | 10 | 81 | 131 | 21 | 760 |
| DHMA-98A-2 | 98A | 8 | 13 | 75 | 135 | 22 | 735 |
| DHMA-98A-3 | 98A | 8 | 11 | 88 | 148 | 27 | 750 |
| DHMA-98A-4 | 98A | 8 | 11 | 79 | 150 | 25 | 760 |
| DHMA-98A-5 | 98A | 8 | 12 | 87 | 153 | 27 | 760 |
Application:
Low temperature chemical sheet, fire hose co-extrusion, ho tmelt adhesive film, fabrics lamination etc,
Dingzhi Polymer provide wide range of raw material, can be widely used in shoe materials, bag materials, sports equipment, medical equipment, the automobile industry, packaging products, wire and cable coating materials, hoses, films, coatings, inks, adhesives, melt spun spandex fibers, artificial leather, bonded clothing, gloves, air blowing products, agricultural greenhouse, air transportation, and national defense industry.
Please contact us for details.