PEEK performance index
test item	test standard	test condition	units	PEEK-1000	PEEK-FC1030	PEEK-G1030	PEEK-C1030
				pure resin	filled carbon fiber	filled 30%	filled 30% carbon fiber
					+graphite+PTFE	glass fiber
					(each 10%)
density	ISO 1183	crystallization	g/cm³	1.3	1.44	1.51	1.4
Bibulous rate (3.2mm thick tensile bar immersion test)	ISO 62-1	24h,23°C	%	0.07	0.06	0.04	0.04
Bibulous rate (3.2mm thick tensile bar immersion test)	ISO 62-1	balance,23°C	%	0.4	0.3	0.4	0.3
tensile strength	ISO-527	bend, 23°C	MPa	100	140	175	260
elongation at break	ISO-527	fracture,23°C	%	45	2.2	2.7	1.7
bending strength	ISO-178	bend, 23°C	MPa	165	190	265	380
flexural modulus	ISO-178	23°C	GPa	4.1	7.8	11.3	23
compression strength	ISO-604	23°C	MPa	125	155	250	300
charpy impact	ISO 179/IeA	notched	KJ/m²	7	5	8	7
strength	ISO 179/IU	no notch	KJ/m²			55	45
cantilever beam impact test	ISO 180/A	notched	KJ/m²	7.5	5	10	9
cantilever beam impact test	ISO 180/U	no totch	KJ/m²	—		60	45
shore hardness	ISO 868	23°C	HD	85	80	88	88
melting point	ISO 11357	—	°C	343	343	343	343
glass transition tempreture	ISO 11357	initial point	°C	143	143	143	143
specific heat capacity	DSC	23°C	KJ/kg °C	2.2	1.7	1.7	1.8
coefficient of thermal expansion	ISO 11359	below Tg along the flow direction	ppm/K	45		18	5
coefficient of thermal expansion	ISO 11359	overtopTg along the flow direction	ppm/K	120		18	6
distortion temperature	ISO 75-f	1.8Mpa	°C	152	300	315	315
thermal conductivity	ISO 22007-4	23°C	W/mK	0.29	0.3	0.3	0.95
dielectrical strength	IEC 60243-1	2mm	KV/mm	23		25	—
dielectric constant	IEC 60250	23°C,1KHz	—	3.1		3.2-3.4	—
dielectric constant	IEC 60250	23°C,50HZ	—	3		—	—
volume resistivity	IEC 60093	23°C, 1V	Ω•cm	1016		1016	—
volume resistivity	IEC 60093	275°C	Ω•cm	109		—	—