White 95% Alumina Ceramics Based Ceramics 20 KV/Mm With High Electrical Insulation And Corrosion Resistance
Product Attributes
| Attribute | Value |
|---|---|
| Material | 95% Alumina Ceramics |
| Color | White |
| Density | 3.6 g/cm³ |
| Dielectric Strength | 20 KV/mm |
| OEM，ODM | Acceptable |
| Origin | WUXI JIANGSU CHINA |
| MOQ | 100 PCS |
| Package | Carton |
Product Description
Alumina ceramics in machinery manufacturing is mainly used to make high-precision mechanical parts, such as ceramic bearings, ceramic sliders, etc., using its high hardness, high strength and low thermal expansion coefficient characteristics.
Technical Specifications
| Material | Unit | A95% Alumina Ceramics | A97% Alumina Ceramics | A99% Alumina Ceramics | A99.7% Alumina Ceramics |
|---|---|---|---|---|---|
| Density | g/cm³ | 3.6 | 3.72 | 3.85 | 3.85 |
| Flexural Strength | Mpa | 290 | 300 | 350 | 350 |
| Compressive Strength | Mpa | 3300 | 3400 | 3600 | 3600 |
| Modulus of Elasticity | Gpa | 340 | 350 | 380 | 380 |
| Impact Resistance | MPam1/2 | 3.9 | 4 | 5 | 5 |
| Weibull Modulus | M | 10 | 10 | 11 | 11 |
| Vickers Hardness | HV0.5 | 1800 | 1850 | 1900 | 1900 |
| Thermal Expansion Coefficient | 10-6K-1 | 5.0-8.3 | 5.0-8.3 | 5.4-8.3 | 5.4-8.3 |
| Thermal Conductivity | W/Mk | 23 | 24 | 27 | 27 |
| Thermal Shock Resistance | △T℃ | 250 | 250 | 270 | 270 |
| Maximum Use Temperature | ℃ | 1600 | 1600 | 1650 | 1650 |
| Volume Resistivity at 20℃ | Ω | ≥1014 | ≥1014 | ≥1014 | ≥1014 |
| Dielectric Strength | KV/mm | 20 | 20 | 25 | 25 |
| Dielectric constant | εr | 10 | 10 | 10 | 10 |
Product Gallery
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Yixing Hengyuan Ceramic Technology Co., Ltd.
Location
Luojian Industrial Park, Dingshu Town, Yixing City, Wuxi City, Jiangsu Province
Contact Person
WU