| Aluminum Pipe/Tube | ||
| Standard | JIS, AiSi, ASTM, GB, DIN, EN etc | |
| Grade |
1000 Series,2000,3000 Series,4000Series,5000Series,6000Series,7000Series,8000Series,9000Series |
|
| Industrial Pure Aluminum | (1050,1060 ,1070, 1100) | |
| Aluminum-copper alloys | (2024(2A12), LY12, LY11, 2A11, 2A14(LD10), 2017, 2A17) | |
| Aluminum-manganese alloys | (3A21, 3003, 3103, 3004, 3005, 3105) | |
| Al-Si alloys | (4A03, 4A11, 4A13, 4A17, 4004, 4032, 4043, 4043A, 4047, 4047A) | |
| Al-Mg alloys | (5052, 5083, 5754, 5005, 5086,5182) | |
| Aluminum Magnesium Silicon Alloys | (6063, 6061, 6060, 6351, 6070, 6181, 6082, 6A02) | |
| Aluminum, Zinc, Magnesium and Copper Alloys | (7075, 7A04, 7A09, 7A52, 7A05) | |
| Surface | Coated, Embossed,Brushed, polished, Anodized,etc | |
| OEM service | Perforated, Cutting special size, Doing flatness, Surface treatment,etc | |
| MOQ | 1 ton | |
| Delivery Time | Within 3 days for our stock size,15-20days for our production | |
| Application | Construction filed, Ships building industry, Decoration, Industry,Manufacture,Machinery and hardware fields, etc | |
| Sample | Free and available | |
| Package | Export standard package: bundled wooden box, suit for all kinds of transport,or be required | |
Available Size Range
| Dimension | Range |
| Outside | 8.0~350mm for Round |
| Diameter | 15x15mm~250x250mm for Square 10x20mm~200x250mm for Rectangle |
| Wall Thickness | 0.5~40mm |
| Length | 1,000~6,000mm |
- Production Process: Extruded, Cold Drawn
- Form & Image: Round, Square, Rectangle
- Surface Finish: Mill Finish, unless otherwise specified
- Surface Protection: Paper interleaved
Temper Designation (For Reference)
| Temper | Definition |
| O | Annealed |
| H14 | Strain Hardened, 1/2 Hard |
| H112 | Slightly strain harden from working at an elevated temperature or from limited amount of cold work |
| T4 | Solution heat-treated and naturally aged |
| T5 | Cooled from an elevated temperature shaping process and then artificially aged |
| T6 | Solution heat-treated and then artificially aged |
| T651 | Solution heat-treated, stress-relieved by stretching a controlled amount and then artificially aged |
| T66 | Solution heat-treated and then artificially aged - mechanical property level higher than T6 achieved through special control of the process (6000 series alloys) |
| T6511 | Solution heated-treaded, stress-relieved by stretching a controlled amount and then artificially aged. Minor straightening is allowed after stretching to comply with standard tolerances |
Chemical Properties of Frequently-used :
| Grade | SI | FE | CU | MN | MG | CR | NI | ZN | AL |
| 1050 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | 0.05 | 99.5 | ||
| 1060 | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | 0.05 | 99.6 | ||
| 1070 | 0.2 | 0.25 | 0.04 | 0.Q3 | 0.03 | 0.04 | 99.7 | ||
| 1100 | Si+Fe:0.95 | 0.05-0.2 | 0.05 | 0.1 | 99 | ||||
| 1200 | Si+Fe:1.00 | 0.05 | 0.05 | 0.1 | 0.05 | 99 | |||
| 1235 | Si+Fe:0.65 | 0.05 | 0.05 | 0.05 | 0.1 | 0.06 | 99.35 | ||
| 3003 | 0.6 | 0.7 | 0.05-0.2 | 1.0-1.5 | 0.1 | remains | |||
| 3004 | 0.3 | 0.7 | 0.25 | 1.0-1.5 | 0.8-1.3 | 0.25 | remains | ||
| 3005 | 0.6 | 0.7 | 0.25 | 1.0-1.5 | 0.20-0.6 | 0.1 | 0.25 | remains | |
| 3105 | 0.6 | 0.7 | 0.3 | 0.30-0.8 | 0.20-0.8 | 0.2 | 0.4 | remains | |
| 3A21 | 0.6 | 0.7 | 0.2 | .0-1.6 | 0.05 | 0.1 | remains | ||
| 5005 | 0.3 | 0.7 | 0.2 | 0.2 | 0.50-1.1 | 0.1 | 0.25 | remains | |
| 5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | 0.1 | remains | |
| 5083 | 0.4 | 0.4 | 0.1 | 0.40-1.0 | 4.0-4.9 | 0.05-0.25 | 0.25 | remains | |
| 5154 | 0.25 | 0.4 | 0.1 | 0.1 | 3.1 -3.9 | 0.15-0.35 | 0.2 | remains | |
| 5182 | 0.2 | 0.35 | 0.15 | 0.20-0.50 | 4.0-5.0 | o.i | 0.25 | remains | |
| 5251 | 0.4 | 0.5 | 0.15 | 0.1-Q.5 | 1.7-2.4 | 0.15 | 0.15 | remains | |
| 5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6-3.6 | 0.3 | 0.2 | remains |
Application
Aluminum alloy tube and pipe can be widely used in construction, machinery, electronics, sports equipment, advertising, transportation, consumer goods, furniture, aviation, military and other applications. We also provide anodizing, bending, welding, polishing and punching service.