Liquid Photosensitive Etching Resist Ink PR-8000 High Resolution Eco Friendly
Price:
xiang tan
MOQ:
200 KG
Delivery Time:
Negotiable
Brand:
JIARUN
Product Description
Liquid photosensitive etch resistance ink, belonging to screen printing ink, has high resolution and is suitable for manufacturing more precise circuits. It can also be used with spray etching or roller coating machines. Additionally, it is applicable to other materials such as copper, stainless steel (#8 mirror steel), and iron.
| Product specifications: | |
| Color: | Indigo |
| solid content | 60% |
| Viscosity: | 100 ~ 150PS ± 20PS (VT-04, 25℃) |
| Curing conditions: | Hot drying: 80℃ x 10 minutes |
| Exposure: 80 – 120mj/cm | |
| Electroplating resistance: | Resistant to copper sulfate, tin-lead, nickel, and various other electroplatings |
| Hardness of cured film: | 2H (pencil hardness) |
| Work process: | |
| Pre-print surface treatment: | cleaning, acid treatment, water washing. |
| Coating: | screen printing, roller coating, spraying |
| Screen printing | MESH: outer layer plating: 120-150 mesh; inner layer etching: 200-250 mesh |
| thickness: | plating: 0.8-1.0 mil; etching: 0.4-0.6 mil. |
| Pre-baking: | first side: 80°C x 10 minutes；second side: 80°C x 15 minutes. |
| Exposure conditions: | 7-8 steps/STOUFFER 21-step exposure scale, outer layer plating: 100-120 mj/cm², inner layer etching: 80-120 mj/cm². |
| Developing: | 1-1.2% sodium carbonate solution, temperature 28 ± 2°C, water washing pressure: 1.5-2.0 kg/cm², developing speed: 40-45 seconds. |
| Etching: | ferric chloride or copper chloride acid etching bath. |
| Plating: | general plating solution. |
| Stripping: | 5-10% sodium hydroxide solution, temperature 40°C, 60 seconds. |
| Thickness: | 10-15μm, 20-25μm. |
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Guangzhou Jiarun New Materials Co., Ltd
Location
No. 18, Meilin Street, Yuancun Fourth Heng Road, Tianhe District, Guangzhou
Contact Person
Kelly Liao