High Temperature Vacuum Induction Melting Furnace 50KG-1000KG For Titanium Alloy

                                      Vacuum induction melting furnace

Vacuum Induction Melting Furnace High Temperature 50KG-1000KG Titanium Alloy Vacuum Induction Melting Furnace for Manufacturing Plant Requirements

 1,Description and main technical indicators of vacuum induction melting furnace

  AE-ZK-1.0L periodic vacuum induction melting furnace is mainly used for medium-frequency induction heating of various high-temperature alloys, iron-based, nickel-based alloys, cobalt-based alloys and certain non-ferrous metals and their alloys under vacuum or inert gas protection. Melting, smelting, casting and molding are carried out according to the principle.

 ,The furnace has a vertical structure. The smelting chamber and the ingot mold chamber are in the same room. Before smelting, the ingot mold is placed in the furnace chamber. After the smelting is completed, the smelted molten steel is poured into the mold through the observation window. After cooling, , break the vacuum, open the side furnace door and take out the cast ingot mold. Start the next batch of work to achieve cycle production

 2. Main Specifications:

 Smelting furnace technical parameters:

 Rated capacity of electric furnace: 1000kg

 Smelting environment: vacuum or inert atmosphere state.

 Melting working temperature: 1600-1700℃

 High temperature: 1750-2000℃ depending on crucible material

 Ultimate vacuum pressure≤6.67X10-2Pa

 Working vacuum degree ≤6.67X10-1Pa

 Air leakage rate ≤50Pa/S

 Empty time ≤50 minutes

 Maximum loadable power: 600KW

 Melting frequency: 1000Hz

 Average melting speed (power delivery from full material to complete melting): 1000Kg/1-1.5h

 Temperature measurement range: 1000-1800℃