PA6 PX08322 BK Flame Retardant Polyamide Nylon Raw Material - 1.53 g/cm³ Density, 180℃ HDT
PA6 PX08322 BK is a high-performance polyamide 6 raw material featuring exceptional wear resistance, high strength, and hydrolytic stability. This mineral-filled, flame-retardant thermoplastic is ideal for demanding industrial applications requiring superior mechanical properties and thermal performance.
Manufacture engine peripheral components including intake manifolds, hood covers, oil pipelines, and pistons.
Used for thrusters, screws, nuts, gaskets, high-pressure seals, oil-resistant gaskets, shells, hoses, cable shears, electromagnetic distribution seats, cold storage equipment, and bearing cages.
Applications in textile machinery, household appliances, electronic devices, construction, sports equipment, household goods, and packaging.
| Property | Value | Unit |
|---|---|---|
| Density | 1.53 | g/cm³ |
| Shrinkage Flow 24hr | 0.5 | % |
| Shrinkage xFlow 24hr | 0.45 | % |
| Tensile Modulus | 11790 | MPa |
| Tensile Strength | 54 | MPa |
| Flexural Strength | 82 | MPa |
| HDT Unannealed (1.8MPa) | 180 | ℃ |
| Heat Conductivity | 2.3 | W/(m * ℃) |
| Property | Value | Unit |
|---|---|---|
| UL94 Flame Rating (1.2mm) | V-0 | - |
| UL94 Flame Rating (3.0mm) | V-0 | - |
| GWIT (1.0mm) | 825 | ℃ |
Injection molding process with recommended dry temperature of 80-90℃. Material supplied in pellet form suitable for various manufacturing applications.