AZ61A Magnesium Alloy Plate 0.6×380×1000mm High Strength to Weight Ratio & Corrosion Resistance
Price:
Negotiable
MOQ:
5kg
Delivery Time:
5-21 days
Brand:
Huona
Product Description
AZ61A Magnesium Alloy Plate (0.6×380×1000mm)
This high-performance wrought Mg-Al-Zn alloy plate from Huona New Material is engineered through precision hot rolling, solution annealing, and controlled cooling processes. As a medium-strength magnesium alloy, it offers an optimal balance of ultra-lightweight properties (density 1.80g/cm³), superior formability, and excellent corrosion resistance—making it ideal for thin-gauge lightweight components in aerospace, 3C electronics, and automotive applications.
Standard Designations & Material Foundation
- Alloy Grade: AZ61A (Mg-Al-Zn system; equivalent to ASTM B107/B107M, UNS M11610)
- Key Specification: 0.6mm thickness × 380mm width × 1000mm length
- Tolerance: Thickness ±0.03mm, width ±0.5mm, length ±2mm
- Chemical Composition (wt%): Al: 5.5-7.0%; Zn: 0.5-1.5%; Mn: 0.15-0.5%; Mg: balance (≥91%)
- Compliant Standards: ASTM B107/B107M, GB/T 5153-2016, RoHS 2.0
- Manufacturer: Huona New Material (ISO 9001 and IATF 16949 certified)
Key Advantages
Ultra-Lightweight & Thin-Gauge Formability
- Extreme Weight Reduction: 33% lighter than 6061 aluminum alloy and 77% lighter than cold-rolled steel
- Excellent Ductility: Elongation ≥15% with bending radius ≤1× thickness
- Lightweight Design: 0.6×380×1000mm plate weighs only ~0.41kg
Optimized Large-Area & Thin-Wall Design
- Wide-Area Coverage: 380mm width eliminates splicing for medium-size components
- Precision Tolerance: Thickness tolerance ±0.03mm ensures uniform wall thickness
Balanced Corrosion Resistance & Mechanical Strength
- Corrosion Protection: Dense oxide film with optional coatings passing 300-hour salt spray testing
- Medium-Strength Performance: Tensile strength ≥240 MPa, yield strength ≥140 MPa
Technical Specifications
| Attribute | Value (Typical) |
|---|---|
| Alloy Grade | AZ61A (O temper, annealed) |
| Dimensions | 0.6mm × 380mm × 1000mm |
| Chemical Composition (wt%) | Al: 5.5-7.0%; Zn: 0.5-1.5%; Mn: 0.15-0.5%; Mg: balance |
| Density | 1.80 g/cm³ |
| Tensile Strength | ≥240 MPa |
| Yield Strength | ≥140 MPa |
| Elongation (25℃) | ≥15% |
| Hardness (HV) | 70-85 |
| Melting Point | ~620℃ |
| Operating Temperature Range | -60℃ to 150℃ |
| Surface Finish | Mill finish (Ra ≤1.2μm); optional chemical conversion coating/anodizing |
Product Specifications
| Item | Specification |
|---|---|
| Supply Form | Single plate (0.6×380×1000mm); batch packaging (50 plates/carton) |
| Surface Treatment | Mill finish; optional chromate-free conversion coating, hard anodizing (5-10μm) |
| Processability | Compatible with stamping, deep drawing, laser cutting, and TIG welding |
| Packaging | PE film wrapping + foam interlayer + wooden pallet |
| Customization | Thickness (0.3-2.0mm); width (100-500mm); length (500-2000mm) |
Typical Application Scenarios
3C Electronics
Thin backplanes for large-size tablets and laptop casings
Thin backplanes for large-size tablets and laptop casings
Aerospace
Drone body panels and wing skins
Drone body panels and wing skins
Automotive Lightweighting
Thin-wall interior trim panels and door handle bases
Thin-wall interior trim panels and door handle bases
Medical Devices
Lightweight housing for portable diagnostic equipment
Lightweight housing for portable diagnostic equipment
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.