CuMn12Ni Precision Manganin Alloy Thick Wire 1.5mm for Instruments & Meters
Price:
Negotiable
MOQ:
5kg
Delivery Time:
5-21 days
Brand:
Huona
Product Description
CuMn12Ni Precision Manganin Alloy Thick Wire 1.5mm for Instruments & Meters
CuMn12Ni manganin wire (1.5mm diameter) from Huona New Material is a high-stability copper-manganese-nickel alloy wire with a bright, uniform surface finish. Composed of Cu (balance) + 11.0-13.0% Mn + 1.5-2.5% Ni with trace stabilizing elements, it is produced via vacuum smelting, hot rolling, multi-pass drawing, and precision annealing.
Standard Designations & Material Foundation
- Alloy Grade: CuMn12Ni
- International Equivalents: UNS C18600, DIN 2.0880, JIS C1860, GB/T 3131-2019 (Mn12Ni)
- Diameter: 1.5mm (±0.01mm); soft/half-hard/hard temper available
- Chemical Composition (wt%): Mn: 11.0-13.0%; Ni: 1.5-2.5%; Cu: balance; Fe ≤0.3%; Pb ≤0.05%; C ≤0.1%
- Compliant Standards: ASTM B124, EN 13602, GB/T 3131-2019, RoHS 2.0
- Manufacturer: Huona New Material, certified to ISO 9001 and ISO 14001
Key Performance Advantages
Ultra-Stable Electrical Performance
- Low TCR & Stable Resistivity: Resistivity = 0.42 μΩ*m (20℃), TCR = ±10×10⁻⁶/℃ (0-100℃)
- High Current-Carrying Capacity: 1.5mm diameter provides excellent current-carrying capability (≥20A continuous)
Excellent Mechanical & Processing Properties
- High Strength & Ductility: Tensile strength ≥500 MPa (hard temper) / ≥320 MPa (soft temper)
- Bright Surface & Good Solderability: Polished bright finish (Ra ≤0.8μm) ensures low contact resistance
Corrosion & Environmental Resistance
- Atmospheric & Mild Corrosion Resistance: Passes 500-hour ASTM B117 salt spray test
- Wide Operating Temperature: -40℃ to 150℃, stable performance in industrial environments
Technical Specifications
| Attribute | Value (Typical) |
|---|---|
| Alloy Grade | CuMn12Ni (soft/half-hard/hard temper) |
| Diameter | 1.5mm (±0.01mm, customizable 0.8-5.0mm) |
| Resistivity (20℃) | 0.42 μΩ*m |
| TCR (0-100℃) | ±10×10⁻⁶/℃ |
| Tensile Strength | ≥500 MPa (hard); ≥320 MPa (soft) |
| Elongation | ≥22% (soft temper) |
| Hardness (HV) | 140-180 (hard); 90-110 (soft) |
| Density | 8.85 g/cm³ |
| Surface Finish | Bright polished (Ra ≤0.8μm) |
| Operating Temperature | -40℃ to 150℃ |
Product Specifications
| Item | Specification |
|---|---|
| Supply Form | Coils (5kg/10kg/25kg per coil) |
| Temper | Soft (annealed), Half-Hard, Hard (as-drawn) |
| Surface Treatment | Bright polished, pickled, or tinned (optional) |
| Processability | Winding, bending, swaging, soldering, welding |
| Packaging | Plastic spool + PE film + carton (anti-oxidation & damage) |
| Customization | Diameter (0.8-5.0mm); length; temper; surface treatment |
Typical Applications
- High-Power Precision Resistors: Wirewound power resistors, load resistors for industrial inverters & power supplies
- Current Shunts: High-current shunts for battery management systems (BMS), power meters, and automotive charging systems
- Industrial Control: Precision resistance elements for PLCs, signal conditioning modules, and temperature compensation circuits
- Automotive & Aerospace: High-stability resistors for automotive electronics and aerospace instrumentation
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Huona (Shanghai) New Material Co., Ltd.
Location
1900 Mudanjiang Road, Baoshan District, 201999, Shanghai, China
Contact Person
Roy