Laminated Farm Tarpaulin Cover Hdpe Tarpaulin Rolls PVC Cover Tarpaulin
| Feature | Value | Standard/Test Method |
|---|---|---|
| Stain Resistant | ||
| Water Absorption | 100% (Weight) | |
| Yarn Count | 500*500 | |
| Coated Type | Coated | |
| Tensile strength | N/50mm | EN 12311-2 Method A ≥ 600 |
| Foldability at low temperature | -25°C | EN 495-5 |
| Artificial ageing (500h) | Grey scale ≥ 3 | EN ISO 4892-2:2006 Method A, cycle 1 EN 20105-A02 |
| Flame retardant | Pass | NPFA-701 |
| Anti-mold | Pass | AATCC 100 |
- Composition: PVC + Polyester Mesh Fabric + PVC
- Thickness: Medium weight
- Weight: 550-650g/m²
- Base Fabric Specification: 500D*500D, 18*17 (Warp*Weft)
- Effective Width: 1.02-3.2M
- Roll Length: 50M / 100M
- Minimum Order Quantity (MOQ): 3000 Meters
- Processing Methods: Sewing, Hot-Air Welding, High-Frequency Welding
- Customization Options: Thickness, Weight, Color, Base Fabric, Width, Roll Length, Special Attributes
Zhejiang Hanlong New Material Co., Ltd is a modernized enterprise professionally engaged in the R&D, design, production and marketing of software for polymer material. We specialize in producing hi-tech new materials including membrane structure materials, tents materials, airtight materials, inflatable materials, cover materials, and various protective materials.
HDPE laminated tarpaulin (190-300g/㎡) adopts hot pressing technology, which is lightweight and economical. The tensile strength is ≥ 600N, and the strength loss after 1500 hours of UV resistance is ≤ 5%. It has moderate breathability and is suitable for silage covering, hay stacks, and temporary shading. PVC coated tarpaulin (500-900g/㎡) adopts coating technology, heavy-duty and durable, with tensile strength ≥ 2800N/5cm, tear strength ≥ 600N, completely waterproof, temperature resistance of -30 ℃ to+70 ℃, suitable for livestock sheds, heavy equipment, and long-term outdoor coverage. Choose HDPE for short-term or limited budget, and PVC for long-term or harsh environments.
HDPE tarpaulin has a static water pressure of ≥ 50kPa (approximately 5000mmH₂O) and a strength retention rate of>95% after 1500 hours of UVB irradiation. The static water pressure of PVC tarpaulin is ≥ 0.3MPa (about 30000mmH₂O), and the strength retention rate is>85% after 2000 hours of xenon lamp aging test. Both have passed the -30 ℃ low-temperature bending test without cracks.
HDPE tear strength ≥ 100N (ISO 4674 A2), no powdering after 3-5 years of field use. The tear strength of PVC in the warp/weft direction reaches 621N/579N (DIN 53363), and it has been used in livestock scenarios for more than 5 years without tearing. The edges are reinforced by high-frequency welding, and the buckle metal washers are reinforced to ensure long-term reliability.