316L 316LN 1/4 Stainless Steel Round Bar Anti Corrosion Acid Alkali Resistant Customizable
| Attribute | Value |
|---|---|
| Support Customization | Support Per Customized |
| Model Numbers | 316L 316LN 304, 304L, 321, 316L, 317L, 309s, 310s |
| Product Category | Stainless steel bars |
| Product Name | Bright High Strength 304, 304L, 321, 316L Stainless Steel Rod Price |
| Application | Highly versatile |
| Chemical Composition | Can be sent for confirmation |
| Product Type | Round steel bar high quality |
| A third-party test report | can be provided according to customer needs |
High quality 316L/316LN stainless steel rods High corrosion resistant building materials Acid and alkali resistant Customizable
| Project | Detailed Description |
|---|---|
| Material Model | 316L (low carbon type), 316LN (nitrogen strengthened type) austenitic stainless steel |
| Core Advantages |
|
| Process standards |
Cold rolling/hot rolling precision processing, dimensional tolerance ±0.1mm Complies with international standards such as GB/T 1220-2007, ASTM A276, etc. |
| Surface treatment | Pickling/polishing/bright annealing, surface roughness can be customized (Ra≤0.8μm) |
| Typical Applications |
|
| Customizable services |
Note: Supports small batch samples and OEM manufacturing, suitable for long-term durability requirements in harsh environments. |
| Category | Parameters | 316L standard value | 316LN standard value | Test Standards |
|---|---|---|---|---|
| Chemical composition | Carbon(C)≤ | 0.03% | 0.03% | ASTM A240 |
| Chromium(Cr) | 16.0-18.0% | 16.0-18.0% | ||
| Nickel(Ni) | 10.0-14.0% | 10.0-14.0% | ||
| Molybdenum(Mo) | 2.0-3.0% | 2.0-3.0% | ||
| Nitrogen(N)≤ | 0.10% | 0.10-0.16% | ||
| Mechanical properties | Tensile strength(MPa)≥ | 485 | 515 | ASTM A276 |
| Yield strength(MPa)≥ | 170 | 205 | ||
| Elongation(%)≥ | 40 | 35 | ||
| Hardness(HB)≤ | 217 | 230 | ||
| Physical properties | Density(g/cm³) | 7.98 | 7.98 | ISO 1183 |
| Melting point(℃) | 1370-1400 | 1370-1400 | ||
| Resistivity(μΩ*m) | 0.74 | 0.74 | ASTM B193 | |
| Corrosion resistance | Pitting resistance equivalent(PREN)* | ≥25 | ≥26 | ASTM G48 |
A third-party test report (SGS/BV, etc.) can be provided according to customer needs.
Additional Notes
Processing suggestions: Solution treatment (1050-1100℃ rapid cooling) is recommended after cold processing to eliminate stress.
Welding performance: 316LN is more suitable for high-strength welded structures due to nitrogen addition.