PC+ABS Bayblend T65 XF Easy Flowing,Covestro Distributor,Low Price
General purpose grades
(PC+ABS)-Blend; Vicat/B 120 temperature = 120 °C; improved flow compared with T65
Rheological properties
|
Eigenschaft |
Prüfbedingung |
Einheit |
Norm |
typischer Wert |
|
|
C |
Melt volume-flow rate |
260℃/5kg |
cm³/10 min |
ISO 1133 |
18 |
|
|
Melt viscosity |
1000 s-1/ 260 °C |
Pa.s |
b.o. ISO 11443-A |
200 |
|
|
Molding shrinkage, parallel |
150x105x3 mm/ 260 °C / MT 80 °C |
% |
b.o. ISO 2577 |
0.5-0.7 |
|
|
Molding shrinkage, normal |
150x105x3 mm/ 260 °C / MT 80 °C |
% |
b.o. ISO 2577 |
0.5-0.7 |
Mechanische Eigenschaften (23 °C/50 % r. F.)
|
Eigenschaft |
Prüfbedingung |
Einheit |
Norm |
typischer Wert |
|
|
C |
Tensile modulus |
1 mm/min |
MPa |
ISO 527-1,-2 |
2350 |
|
C |
Yield stress |
50 mm/min |
MPa |
ISO 527-1,-2 |
54 |
|
C |
Yield strain |
50 mm/min |
% |
ISO 527-1,-2 |
4.4 |
|
|
Stress at break |
50 mm/min |
MPa |
ISO 527-1,-2 |
47 |
|
|
Stress at break |
50 mm/min |
% |
ISO 527-1,-2 |
>50 |
|
|
Flexural modulus |
2 mm/min |
MPa |
ISO 178 |
2350 |
|
|
Flexural stress at 3.5 % strain |
2 mm/min |
MPa |
ISO 178 |
73 |
|
|
Flexural strength |
2 mm/min |
MPa |
ISO 178 |
84 |
|
|
Izod impact strength |
23°C |
kJ/m² |
ISO 180/U |
N |
|
|
Izod impact strength |
-30 °C |
kJ/m² |
ISO 180/U |
N |
|
|
Izod notched impact strength |
23 °C |
kJ/m² |
ISO 180/A |
48 |
|
|
Izod notched impact strength |
-30 °C |
kJ/m² |
ISO 180/A |
35 |
|
C |
Charpy notched impact strength |
23 °C |
kJ/m² |
ISO 179/1eA |
50 |
|
C |
Charpy notched impact strength |
-30 °C |
kJ/m² |
ISO 179/1eA |
36 |
Resins wholesale,Factory-Direct supply,Certified supplier
Main Product: PC,PC/ABS,PC/PET,PC/PBT
Customized Services: Modified, Color matching, Production technical support
Several Warehouse: Guang zhou, Dong guan, Shen zhen, Hong kong
Get in Touch for More Info! and Speak to Our Manager Today!
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.