Hot Rolled Square Hollow Section for Heavy Duty Construction
Hot-Rolled Square Hollow Section for Heavy-Duty Construction
Specifications
Hot rolled steel tubes are manufactured by passing sheet metal through rollers to achieve specific physical dimensions. The finished product has a rough surface finish with radiused corners and either a welded or seamless construction.
| American Standard | Standard Name |
| A500/A500M | Standard Specification for Cold-Formed Welded and Seamless Carbon Steel Structural Tubing in Rounds and Shapes |
Hot-Rolled Square Tube Chemical Composition
Sources American Standard A500 / A500M TABLE 1 Chemical Requirements
| Element | Composition, % | |||
| Grades A, B and D | Grace C | |||
| Heat | Product | Heat | Product | |
| Analysis | Analysis | Analysis | Analysis | |
| Carbon, max A | 0.26 | 0.3 | 0.23 | 0.27 |
| Manganese, max A | 1.35 | 1.4 | 1.35 | 1.4 |
| Phosphorus, max | 0.035 | 0.045 | 0.035 | 0.045 |
| Sulfur, max | 0.035 | 0.045 | 0.035 | 0.045 |
| Copper, min B | 0.2 | 0.18 | 0.2 | 0.18 |
| A For each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.06 percentage point above the specified maximum for manganese is permitted, up to a maximum of 1.50% by heat analysis and 1.60% by product analysis. B If copper-containing steel is specified in the purchase order. |
||||
Hot-Rolled Square Tube Mechanical Properties
Sources American Standard A500 / A500M TABLE 2 Tensile Requirements
| Round structural tubing | ||||
| Grade A | Grade B | Grade C | Grade D | |
| Tensile strength, min, psi (MPa) | 45,000 (310) | 58,000 (400) | 62,000 (425) | 58,000 (400) |
| Yield strength, min, psi, (MPa) | 33,000 (230) | 42,000 (290) | 46,000 (315) | 36,000 (250) |
| Elongation in 2 in. (50 mm), min, %D | 25A | 23B | 21C | 23B |
| Shaped structural tubing | ||||
| Grade A | Grade B | Grade C | Grade D | |
| Tensile strength, min, psi (MPa) | 45,000 (310) | 58,000 (400) | 62,000 (425) | 58,000 (400) |
| Yield strength, min, psi, (MPa) | 39,000 (270) | 46,000 (315) | 50,000 (345) | 36,000 (250) |
| Elongation in 2 in. (50 mm), min, %D | 25A | 23B | 21C | 23B |
| A Applies to specified wall thicknesses (t) equal to or greater than 0.120 in. (3.05 mm). For lighter specified wall thicknesses, the minimum elongation values shall be calculated by the formula: percent elongation in 2 in. (50mm) = 56t + 17.5, rounded to the nearest percent. For A500M use the following formula: 2.2t + 17.5, rounded to the nearest percent. B Applies to specified wall thicknesses (t) equal to or greater than 0.180 in. (4.57 mm). For lighter specified wall thicknesses, the minimum elongation values shall be calculated by the formula: percent elongation in 2 in. (50 mm) = 61t + 12, rounded to the nearest percent. For A500M use the following formula: 2.4t + 12, rounded to the nearest percent. C Applies to specified wall thicknesses (t) equal to or greater than 0.120 in. (3.05 mm). For lighter specified wall thicknesses, the minimum elongation values shall be by agreement with the manufacturer. D The minimum elongation values specified apply only to tests performed prior to shipment of the tubing. |
||||
Hot-Rolled Square Tube Manufacturing Process
Hot-Rolled Square Tube Application
- Structural Frameworks in Construction
- Infrastructure and Civil Engineering
- Industrial Manufacturing Facilities
- Energy and Power Generation
- Transportation and Heavy Vehicles
- Mining and Heavy Industry
- Agricultural and Farming Infrastructure
- Shipbuilding and Marine Applications
- Storage and Warehousing
- Foundations and Piling
- General Fabrication and Welding
Hot-Rolled Square Tube Packing & Loading
Hollow Section is transported in containers
Hollow Section is transported in containers