0.012-0.1mm 3003 H13 Aluminum foil for honeycomb foil
Price:
2900-3100 sud/ton
MOQ:
1ton
Delivery Time:
7-15work days
Brand:
Yongsheng
Product Description
0.012-0.1mm 3003 H13 Aluminum Foil for Honeycomb Applications
Specialized aluminum foil designed for manufacturing high-performance honeycomb core structures used across various industrial applications.
Product Specifications
| Alloy | 3003, etc |
| Temper | H18, H19, etc |
| Thickness | 0.012-0.1mm |
| Width | 180-1350mm |
| Length | Customer Requirement |
| Performance | Tensile strength >240 MPa, elongation after break >1% |
| Port | ShangHai, TianJin, QingDao |
| Sample | Free |
3003 H18 Alloy Chemical Properties
- Composition basis: Aluminum-manganese alloy (Mn about 1.0-1.5%)
- Strengthening mechanism: Pure cold work hardening (non-heat treatment strengthening)
3003 H18 Alloy Physical Properties
- High strength: High strength level achieved through cold working
- High hardness: High surface hardness and relatively good wear resistance
- Low ductility: Poor plasticity and limited formability
- Excellent corrosion resistance in atmospheric and chemical environments
- Good weldability with heat affected zone softening
- Good processability with appropriate tooling
Honeycomb Core Manufacturing Process
Precision automated process transforming aluminum foil into continuous hexagonal honeycomb cell structures through specialized forming and bonding techniques.
1. Aluminum Foil Preparation
Selection of 3003 grade aluminum foil coils with specific thickness requirements. Surface preparation includes degreasing and chemical treatment to enhance adhesive bonding.
2. Gluing
Application of high-strength adhesive in parallel stripes using precision roller coating or spraying methods to ensure uniform, continuous application.
3. Corrugation Forming
Flat aluminum foil passes through precision corrugation rollers to create continuous wave shapes with controlled peak distance and height.
4. Lamination and Stacking
Precise alignment and stacking of multiple corrugated aluminum foil layers with peak-to-glue-stripe positioning.
5. High Temperature Curing
Hot press application melts and solidifies adhesive, creating strong bonding points between adjacent aluminum foil layers.
6. Honeycomb Block Formation
Cured laminate forms integrated aluminum block with regular internal pore structure, known as honeycomb core blank.
7. Stretching and Unfolding
Controlled tension application perpendicular to corrugation direction evenly spreads cellular structures into three-dimensional hexagonal honeycomb configuration.
Technical Parameters
| Alloy | 3003, etc |
| Temper | H18, H19, etc |
| Thickness | 0.012-0.1mm |
| Width | 180-1350 mm (tolerance:± 1.0mm) |
| Length | As per your requirements |
| Feature | Eco-friendly |
| Package | Standard Sea-worthy Packing |
| Type | High Purity Aluminium Foil Coil |
| Color | Silver |
| Shape | Alu Coil |
| Hardness | O/HO |
| Conductivity (% IACS) | ≥61.5 |
| Elongation (%) | > 23 |
| Application | Industry, Decoration, Building, Packing, Pressing, Etc. |
| Surface treatment | Mill Finish, Coated, Powder Coated, Anodized, Polished mirror, Embossed, Etc. |
Product Gallery
Industry Applications
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Henan Yongsheng Aluminum Industry Co.,Ltd.
Location
Jinshui District, Zhengzhou City, Henan Province
Contact Person
Eric