0.5mm Pitch H2.0 FPC Easy On Right Angle SMT Connectors CAX CAX AFC01 28XCB H2.0 Featuring LCP Housing
Price:
Negotiable
MOQ:
Negotiable
Delivery Time:
Negotiable
Product Description
Product Overview
This specification covers the 0.5mm Pitch H=2.0 FPC Easy-on R/A SMT type connectors series. Designed for reliable electrical connections, these connectors feature a LCP housing and actuator, with phosphor bronze terminals and fitting nails. They are suitable for a wide operating temperature range and offer robust performance in various environmental conditions, including vibration, shock, and humidity. The easy-on design facilitates simple FPC insertion and removal.
Product Attributes
- Brand: ZHE JIANG CHUANG DU ELECTRONICS CO.,LTD
- Product Series: 0.5mm Pitch H=2.0 FPC Easy-on R/A SMT type connectors
- Housing Material: LCP (White, UL94V-0 Flammability Rating)
- Actuator Material: LCP (Black, UL94V-0 Flammability Rating)
- Terminal Material: Phosphor Bronze
- Fitting Nail Material: Phosphor Bronze
- Pitch: 0.5mm
- Height: 2.0mm
- Type: Easy-on, Right Angle (R/A), SMT
Technical Specifications
| Category | Item | Test Condition | Specification |
|---|---|---|---|
| Rating | Operating Voltage (Max.) | 50V AC | |
| Current Rating (Max.) | (*Including terminal temperature rise) | 0.5A DC | |
| Operating Temperature Range | -55C ~ +85C | ||
| Rating | Operating Humidity Range | Relative humidity 90% max. | |
| Storage Temperature Range | -10C ~ +50C | ||
| Rating | Storage Humidity Range | Relative humidity 90% max. | |
| Electrical Performance | Contact Resistance | Mate applicable FPC, 20mV Max, 10mA (EIA-364-23) | 30 m Max. |
| Insulation Resistance | Mate applicable FPC, 500V DC between adjacent terminals or ground (EIA-364-21) | 500 M Min. | |
| Dielectric Strength | Mate applicable FPC, 250V AC(rms) for 1 minute between adjacent terminals or ground (EIA-364-20) | No Breakdown | |
| Mechanical Performance | FPC Retention Force | Insert actuator, pull FPC at 253mm/min | Pos.x 0.30N Min. |
| Terminal Retention Force | Axial pull out force on terminal assembled in housing at 253mm/min | 3N Min. | |
| Fitting Nail Retention Force | Axial pull out force on fitting nail assembled in housing at 253mm/min | 1.0N Min. | |
| Environmental Performance and Others | Durability | Insert and withdraw actuator up to 20 cycles at | Contact Resistance: 60m Max. |
| Temperature Rise | Measure contact point temperature rise when max rated current passed through FPC (EIA-364-70 Method 2) | 30C Max. | |
| Vibration | DC 1mA, 1.5mm amplitude, 10~55~10 Hz for 2 hours in X, Y, Z axes (EIA-364-28 Condition I) | Appearance: No Damage Contact Resistance: 60m Max. Discontinuity: 1sec Max. | |
| Environmental Performance and Others | Shock | DC 1mA, 490m/s {50G} for 3 times in 6 directions (EIA-364-27, test condition A) | Appearance: No Damage Contact Resistance: 60m Max. Discontinuity: 1sec Max. |
| Heat Resistance | Mate FPC, expose to 852C for 96 hours, then condition at room temp. | Appearance: No Damage Contact Resistance: 60m Max. | |
| Cold Resistance | Mate FPC, expose to -402C for 96 hours, then condition at room temp. | Appearance: No Damage Contact Resistance: 60m Max. | |
| Environmental Performance and Others | Humidity | Mate FPC, expose to 602C, 90-95% RH for 96 hours, then condition at room temp. | Appearance: No Damage Contact Resistance: 60m Max. Dielectric Strength: No Breakdown Insulation Resistance: 30 M Min. |
| Temperature Cycling | Mate FPC, 5 cycles of -553C (30 min) to +853C (30 min), then condition at room temp. | Appearance: No Damage Contact Resistance: 60m Max. | |
| Salt Spray | Mate FPC, 51% NaCl solution, 352C for 484 hours, then rinse and dry. | Appearance: No Damage Contact Resistance: 60m Max. | |
| Environmental Performance and Others | SO2 Gas | Mate FPC, expose to 505 ppm SO2 gas at 402C for 24 hours. | Appearance: No Damage Contact Resistance: 60m Max. |
| NH3 Gas | Mate FPC, 40 minutes exposure to NH3 gas from 28% Ammonia solution. | Appearance: No Damage Contact Resistance: 60m Max. | |
| Soldering | Solderability | Immersion of terminals/nails in molten solder (2455C) for 30.5 seconds. | Solder Wetting: 75% of immersed area must show no voids, pinholes. |
| Resistance to Soldering Heat | Soldering iron method: 0.2mm from terminal tip, 5 seconds Max., 370~400C | Appearance: No Damage |
Infrared Reflow Condition
Temperature on Board Pattern Side:
| Stage | Time | Temperature (C) |
|---|---|---|
| Start (Pre-Heat) | (60sec) | 50 - 150C MAX. |
| (60~90sec) | 200C | |
| (30sec) | 230C MIN. / 20~40sec | |
| Peak Temp | 3sec. or less | 250C MAX. |
Operation Instructions
Easy-on Type Operation:
- Step 1: Use the thumb or forefinger to lift the top cover upwards.
- Step 2: Insert the FPC with conductive side down, parallel to the connector.
- Step 3: Press the top cover lightly and rotate down until the FPC is fully inserted and secured.
- Step 4: To withdraw the FPC, lift the top cover carefully and then withdraw the FPC.
Warnings:
- The rotation angle of the cover should not exceed 120 degrees.
- Inserting the FPC at an excessive angle may cause electrical discontinuity.
- Upward pulling force should not exceed 0.04N/pin max.
- Do not use excessive force when opening the connector's top cover to avoid touching the terminals.
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
Hefei Purple Horn E-Commerce Co., Ltd.
Location
Room 1306B, Building A, Xindi Center, Qimen Road, Hefei City, Anhui Province
Contact Person
Sellina